SABIC Innovative Plastics LNP STAT-KON ZEF061XC PPO (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON ZEF061XC PPO (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STATKON* ZEF061XC is a compound based on Polyphenyleneoxide resin containing Glass Fiber, Milled Carbon Fiber and Flame Retardant. Added Features include: Electrically Conductive
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Water Absorption | 0.11 % @Time 86400 sec |
0.11 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 97.0 MPa | 14100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.3 % | 1.3 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 12.1 GPa | 1750 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 124 MPa | 18000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 9.50 GPa | 1380 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
13.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 88.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
48.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-1 @Thickness 3.00 mm |
V-1 @Thickness 0.118 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1000 - 1.00e+6 ohm | 1000 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Ferro IX 2405 Dental Glass
- Gouda Vuurvast GOLITE 1.2.4. MIX GM Refractory Insulating Castable
- Lehmann & Voss LUVOCOM® 1100-8326 Polyether sulfone, with carbon fiber, PTFE, lubricant modified
- Solvay Chemicals SOLKANE® 141b Surface Treatment Agent
- Techmer ES Luriblend® PA6/6 TL20 HS L Nylon 66
- Teknor Apex Monprene® MP 1079E Thermoplastic Elastomer
- A. Schulman POLYBATCH™ Yellow 2946ST Concentrate Based In Polyethylene
- CMW® 3950 AMS-T-21014 ASTM B777 High Density Machinable Tungsten
- Addiplast Addinyl B2 ZV 50 Nylon 6, 50% Glass Filled
- Aremco Aremco-Bond™ 2310 High Performance Epoxide
Copyright © lookpolymers.com All Rights Reserved