SABIC Innovative Plastics LNP STAT-KON ZE004 PPO
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON ZE004 PPO.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* ZE004 is a compound based on PPO resin containing 20% Carbon Fiber. Added feature of this grade includes: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D792 |
| 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0053 cm/cm @Time 86400 sec |
0.0053 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 103 MPa | 14900 psi | ISO 527 |
| 104 MPa | 15100 psi | ASTM D638 | |
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | ISO 527 |
| 80.0 MPa | 11600 psi | ASTM D638 | |
| Elongation at Break | 0.50 % | 0.50 % | ASTM D638 |
| 0.90 % | 0.90 % | ISO 527 | |
| Tensile Modulus | 14.72 GPa | 2135 ksi | 1 mm/min; ISO 527 |
| 24.82 GPa | 3600 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 151 MPa | 21900 psi | ISO 178 |
| 179 MPa | 26000 psi | ASTM D790 | |
| Flexural Modulus | 12.7 GPa | 1840 ksi | ISO 178 |
| 24.13 GPa | 3500 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.99 J/cm | 5.60 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 48.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 48.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 37.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 139 °C @Thickness 3.20 mm |
282 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 137 °C @Thickness 3.20 mm |
279 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Quadrant EPP Duratron® PEI U1000 Extruded Unfilled Polyetherimide (ASTM Product Data Sheet)
- Karina E 65/200 Clear PVC Compound
- SABIC Innovative Plastics NORYL SA120 PPE (Asia Pacific)
- Westlake Plastics Lennite® Ultra High Molecular Weight Polyethylene
- Ecomass® 1050TU96 Tungsten Filled Polyamide
- Eurotec® Tecomid® NA40 GR50 NL RM PA6.6, 50% glass fiber reinforced, MoS2 modified, natural
- Arlon 940-10Rxx-P1 0.040" (1.02 mm) Self-Fusing Silicone Tape
- Clariant Renol 66G33-L Nylon 66, 33% Glass Fiber Reinforced, Lubricated
Copyright © lookpolymers.com All Rights Reserved