SABIC Innovative Plastics LNP STAT-KON MX12407C PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON MX12407C PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* MX12407C is a compound based on Polypropylene resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding System.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.980 g/cc | 0.980 g/cc | ASTM D792 |
| Density | 0.974 g/cc | 0.0352 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0200 % | 0.0200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.017 cm/cm @Time 86400 sec |
0.017 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm @Time 86400 sec |
0.017 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 19.0 MPa | 2760 psi | Type I, 5 mm/min; ASTM D638 |
| 20.0 MPa | 2900 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | 5 mm/min; ISO 527 |
| 22.0 MPa | 3190 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 297 % | 297 % | Type I, 5 mm/min; ASTM D638 |
| 666 % | 666 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 8.6 % | 8.6 % | 5 mm/min; ISO 527 |
| 10 % | 10 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 0.980 GPa | 142 ksi | 1 mm/min; ISO 527 |
| 1.42 GPa | 206 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 23.0 MPa | 3340 psi | ISO 178 |
| Flexural Yield Strength | 24.0 MPa | 3480 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 0.990 GPa | 144 ksi | 2 mm/min; ISO 178 |
| 1.02 GPa | 148 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 8.73 J/cm | 16.4 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 57.0 kJ/m² | 27.1 ft-lb/in² | 80*10*4; ISO 180/1A |
| Dart Drop, Total Energy | 31.0 J @Temperature 23.0 °C |
22.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 35.0 J | 25.8 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 117 µm/m-°C @Temperature -30.0 - 30.0 °C |
65.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 126 µm/m-°C @Temperature -30.0 - 30.0 °C |
70.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 77.0 °C | 171 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 90.0 °C @Thickness 3.20 mm |
194 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C | 120 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 49.0 °C @Thickness 3.20 mm |
120 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1000 - 1.00e+6 ohm-cm | 1000 - 1.00e+6 ohm-cm | ASTM D257 |
| Surface Resistance | 1000 - 1.00e+6 ohm | 1000 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- PolyOne Syncure™ S1000B Polyethylene, Crosslinked (XLPE)
- Polymax® Maxelast® P1870 TPE, PP Overmold or Standalone use
- Kazanorgsintez E-15 Petroleum Resin
- Global GPP-240C 40% Glass Reinforced, Chemically Coupled Impact Polypropylene
- Techmer ES Luriblend® PA6/6 CF20 TS15 BK 20% Carbon Filled
- ConocoPhillips SynXPA® 32 Turbine Oil
- ATI Allegheny Ludlum Stainless Steel AL-6XN® Alloy (UNS N08367), 50% Cold Work
- Plastcom SLOVALEN PH 51 T 10 Polypropylene Homopolymer, 10% Mineral Filled
Copyright © lookpolymers.com All Rights Reserved