SABIC Innovative Plastics LNP STAT-KON KEP33 Acetal (Asia Pacific)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON KEP33 Acetal (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* KEP33 is a compound based on Acetal resin containing Silicone, Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 |
| 1.473 g/cc | 0.05322 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.210 % | 0.210 % | 50% RH, 24 hrs; ASTM D570 |
| 0.320 % | 0.320 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.00070 - 0.00090 cm/cm @Time 86400 sec |
0.00070 - 0.00090 in/in @Time 24.0 hour |
ISO 294 |
| 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 74.0 MPa | 10700 psi | ISO 527 |
| 77.0 MPa | 11200 psi | ASTM D638 | |
| Elongation at Break | 1.0 % | 1.0 % | ISO 527 |
| 1.1 % | 1.1 % | ASTM D638 | |
| Tensile Modulus | 10.17 GPa | 1475 ksi | 1 mm/min; ISO 527 |
| 10.2 GPa | 1480 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 106 MPa | 15400 psi | ISO 178 |
| 114 MPa | 16500 psi | ASTM D790 | |
| Flexural Modulus | 7.14 GPa | 1040 ksi | ASTM D790 |
| 8.27 GPa | 1200 ksi | ISO 178 | |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.28 J/cm | 2.40 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J | 5.16 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.36 | 0.36 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.31 | 0.31 | ASTM D3702 Modified |
| K (wear) Factor | 407 x 10-8 mm³/N-M | 202 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 155 °C | 311 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 66.0 °C @Thickness 3.20 mm |
151 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10 - 10000 ohm-cm | 10 - 10000 ohm-cm | ASTM D257 |
| Surface Resistance | 10 - 10000 ohm | 10 - 10000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Gwent Electronic Materials C2030529D3 Gold Via Ink
- SABIC Innovative Plastics LNP LUBRICOMP RFL36S PA 66 (Europe-Africa-Middle East)
- Samyang Triloy® 210NHF Polymer Alloy, Flame Retardancy (Non-Halogen)
- EMS-Grivory Grivory® HT1V-3 FWA black 9225 PA6T/6I-GF30
- BASF Caprolactam Liquid
- 3M XG5110 General Purpose Double Coated Tape
- Aaron Industries AAROPRENE® GFIPP 2010 High Impact Glass Filled Polypropylene
- ExxonMobil Oppalyte™ 40MD447 OPP Film
- BASF Novolen® 1102 L Polypropylene
Copyright © lookpolymers.com All Rights Reserved