- Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled
- EPICHEM Epilac R ABS 17% GF ABS, 17% Glass Fiber
EPICHEM Epilac R ABS 17% GF ABS, 17% Glass Fiber
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled |
| Manufacturer | EPICHEM srl |
| Trade Name | Epilac |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EPICHEM Epilac R ABS 17% GF ABS, 17% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics: 17% glass fibre filled
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D792, ISO 1183 |
| Water Absorption | 0.25 % @Temperature 23.0 °C |
0.25 % @Temperature 73.4 °F |
24h; ASTM D570, ISO 62 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 103 | 103 | ASTM D785, ISO 2039/2 |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | ASTM D638, ISO R527 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638, ISO R527 |
| Flexural Strength | 95.0 MPa | 13800 psi | ASTM D790, ISO 178 |
| Flexural Modulus | 5.45 GPa | 790 ksi | ASTM D790, ISO 178 |
| Izod Impact, Notched | 0.400 J/cm @Thickness 3.20 mm, Temperature -30.0 °C |
0.749 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F |
ASTM D256, ISO 180/4a |
| 0.500 J/cm @Thickness 3.20 mm, Temperature 0.000 °C |
0.937 ft-lb/in @Thickness 0.126 in, Temperature 32.0 °F |
ASTM D256, ISO 180/4a | |
| 0.700 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.31 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256, ISO 180/4a |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | >= 80.0 °C | >= 176 °F | BS 3456, IEC 335 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648, ISO 75 |
| Vicat Softening Point | 100 °C @Load 5.00 kg |
212 °F @Load 11.0 lb |
120°C/min; ASTM D1525/B, ISO 306/B |
| 110 °C @Load 0.999 kg |
230 °F @Load 2.20 lb |
120°C/min; ASTM D1525/A, ISO 306/A | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Glow Wire Test | 650 °C @Thickness 3.20 mm |
1200 °F @Thickness 0.126 in |
VDE 0471/P2-4, IEC 695 |
| 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
VDE 0471/P2-4, IEC 695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257, IEC 93 |
| Dielectric Constant | 3.4 @Frequency 1000 Hz |
3.4 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | ASTM D149, IEC 243 |
| Dissipation Factor | 0.020 @Frequency 1000 Hz |
0.020 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | VDE 0303-P1, IEC 112 |
Users viewing this material also viewed the following:
- Nye Lubricants 951 (RL) Synthetic Oil
- Resinlab® CYNERGY CA6206 Adhesive
- H.C. Starck Amperit® 705.1 Fused Chromium Oxide 96.0 % (Cr2O3)
- Special Metals Electroformed Nickel, 13 Micron (0.5 mil) Foil, Electroformed and Annealed
- Teknor Apex APEX® 3601-85 Polyvinyl Chloride, Flexible
- SABIC Innovative Plastics NORYL PCN2615H PPE+PS (Asia Pacific)
- Ensinger Tecapeek® CLASSIX XRO Polyetheretherketone (PEEK)
- Arkema Group Lucalor® RB 8065 CPVC, Pipe Grade
- 3M Nextel™ AF-10 Aerospace Woven Fabric 312
Copyright © lookpolymers.com All Rights Reserved