SABIC Innovative Plastics LNP STAT-KON DEP42E PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DEP42E PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DEP42E is a compound based on Polycarbonate resin containing Silicone, PTFE, Carbon Fiber. Added features of this material include: Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.150 % | 0.150 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0019 cm/cm @Time 86400 sec |
0.0019 in/in @Time 24.0 hour |
ISO 294 |
| 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0051 cm/cm @Time 86400 sec |
0.0051 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 104 MPa | 15100 psi | ASTM D638 |
| 105 MPa | 15200 psi | ISO 527 | |
| Elongation at Break | 1.9 % | 1.9 % | ISO 527 |
| 2.0 % | 2.0 % | ASTM D638 | |
| Tensile Modulus | 8.58 GPa | 1240 ksi | 1 mm/min; ISO 527 |
| 8.75 GPa | 1270 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
| 161 MPa | 23400 psi | ASTM D790 | |
| Flexural Modulus | 7.65 GPa | 1110 ksi | ASTM D790 |
| 8.60 GPa | 1250 ksi | ISO 178 | |
| Izod Impact, Notched | 0.810 J/cm | 1.52 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.26 J/cm | 9.85 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 26.0 kJ/m² | 12.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 12.0 J | 8.85 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 32.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
18.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 32.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
18.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 34.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
19.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 34.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
19.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 146 °C | 295 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 142 °C | 288 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Oxford Polymers PEEK-20CF-Black PEEK, 20% Carbon Fiber Reinforced
- Quadrant EPP Nylatron® WP PA (ASTM Product Data Sheet)
- Reltek BONDiT™ B-482TH Adhesive and Sealant
- SABIC Innovative Plastics ULTEM 4000 PEI (Europe-Africa-Middle East)
- Spartech Korad® SP-9071 FR/ABS Flame Retardant Sheet
- Solvay LUBRHOPHOS® LB 400 E Surfactant
- Total PPC 9712 Polypropylene, Heterophasic Copolymer
- Hexcel® HexWeb® CR-PAA™ 1/4-5056-0.0025 Phosphoric Acid Anodized Aluminum Honeycomb
- Dow Corning SYL-OFF® PMCPSL 50 Release Modifier
- Azdel SuperLite® SL550800-100 PP Resin Matrix / 55% Glass Fiber (2.5 mm Molded Thickness)
Copyright © lookpolymers.com All Rights Reserved