SABIC Innovative Plastics LNP THERMOCOMP 2F006 ETFE
| Category | Polymer , Thermoplastic , Fluoropolymer , ETFE/ECTFE |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP 2F006 ETFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* 2F006 is a compound based on ETFE containing 30% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.90 g/cc | 1.90 g/cc | ASTM D792 |
| Density | 1.91 g/cc | 0.0690 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0200 % | 0.0200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm @Time 86400 sec |
0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 74.0 MPa | 10700 psi | 5 mm/min; ISO 527 |
| 79.0 MPa | 11500 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | 5 mm/min; ISO 527 |
| 80.0 MPa | 11600 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 5.0 % | 5.0 % | 5 mm/min; ISO 527 |
| 5.2 % | 5.2 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 4.6 % | 4.6 % | 5 mm/min; ISO 527 |
| 4.9 % | 4.9 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 8.08 GPa | 1170 ksi | 1 mm/min; ISO 527 |
| 8.93 GPa | 1300 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 115 MPa | 16700 psi | 2 mm/min; ISO 178 |
| 117 MPa | 17000 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 7.52 GPa | 1090 ksi | 2 mm/min; ISO 178 |
| 7.64 GPa | 1110 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 3.44 J/cm | 6.44 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.4 J/cm | 19.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 67.0 kJ/m² | 31.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 17.0 J @Temperature 23.0 °C |
12.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 8.00 J | 5.90 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 26.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
14.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 75.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 246 °C | 475 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 254 °C @Thickness 3.20 mm |
489 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 187 °C | 369 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 215 °C @Thickness 3.20 mm |
419 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nanocyl EPOCYL™ NC R1MY-04 Master Batch Liquid tetrafunctional epoxy Resin for solvent based Formulation Purposes: Dilution Factor 6
- Outokumpu 4021 Martensitic Stainless Steel
- Reade Advanced Materials Bentonite Powder (BaTiSi3O9)
- Haynes Multimet® alloy, 1.32 mm thick sheet, 1177°C heat treatment, rapid air cooled
- China Tungsten ST1365 PM Antifriction Parts
- 3M 31U26C/UV Protective UV Tape
- 3M Scotchcal™ 8000-14 Graphic Film
- Axiall 38900 Wire & Cable Flexible PVC
- MV Labs CE300 Ce2(CO3)3·xH2O Cerium(III) carbonate hydrate
- Fainplast Compounds CL 0133/R Flexible PVC, Sheathing
Copyright © lookpolymers.com All Rights Reserved