SABIC Innovative Plastics LNP STAT-KON DE0049P PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DE0049P PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* DE0049P is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Exceptional Processing, Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ASTM D792 |
| 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0014 cm/cm @Time 86400 sec |
0.0014 in/in @Time 24.0 hour |
ISO 294 |
| 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0056 cm/cm @Time 86400 sec |
0.0056 in/in @Time 24.0 hour |
ISO 294 |
| 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 132 MPa | 19100 psi | ISO 527 |
| 137 MPa | 19900 psi | ASTM D638 | |
| Elongation at Break | 0.90 % | 0.90 % | ASTM D638 |
| 1.3 % | 1.3 % | ISO 527 | |
| Tensile Modulus | 15.96 GPa | 2315 ksi | 1 mm/min; ISO 527 |
| 16.54 GPa | 2399 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
| 219 MPa | 31800 psi | ISO 178 | |
| Flexural Modulus | 12.41 GPa | 1800 ksi | ASTM D790 |
| 13.2 GPa | 1910 ksi | ISO 178 | |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.32 J/cm | 8.09 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 34.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
19.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 35.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
19.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 32.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
18.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 33.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
18.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 289 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 143 °C @Thickness 3.20 mm |
289 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C | 282 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® LC120 PC (Asia Pacific)
- Polimeri Europa Dutral® OCP 2530 PL Ethylene - Propylene
- PolyOne Geon™ 130 Series 138 Polyvinyl Chloride Copolymer (PVC Copolymer)
- Lehmann & Voss LUVOCOM® 1105/GF/14 PEEK, with glass fiber
- LATI Latilub 80-10T K/15 PPS, 15% Carbon Fiber Reinforced, PTFE Filled
- Teknor Apex Beetle® MD82 Nylon 6, Non-halogenated, Dry
- A. Schulman POLYBATCH™ Bright White P80514PF Concentrate Based In Polypropylene
- CIMBAR RiverCal™ 8105 & 8105C Calcium Carbonate (CaCO3)
- BASF Ultramid® S3EG6 Balance 30% Glass Filled PA 610 (Dry)
- 3M Scotchcast™ 2131 Flame-Retardant Compound
Copyright © lookpolymers.com All Rights Reserved