SABIC Innovative Plastics LNP STAT-KON DE003E PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DE003E PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* DE003E is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | on Tensile Bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 134 MPa | 19400 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.6 % | 1.6 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 12.2 GPa | 1770 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 184 MPa | 26700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 10.8 GPa | 1570 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
5.56 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 67.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
37.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 289 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 15 T 25 LTS PA6, 15% glass fibre, 25% mineral filling
- Lehmann & Voss LUVOCOM® 1106-7622 Polyether imide, with carbon fiber
- Lehmann & Voss LUVOCOM® 1301-7648/BK PPS, linear, with glass fiber
- Lanxess Pocan® B 2505 000000 PBT
- SABIC Innovative Plastics Xenoy® 6380U PBT+PET (Asia Pacific)
- Samyang Triel® 5501BM Thermoplastics Polyetherester Elastomer, Blow Molding
- Teknor Apex Monprene® MP-1848R Thermoplastic Elastomer
- Sinotek Materials WT85-Q Amorphous Graphite Briquettes
- Akro-Plastic Akroloy® PA GF 40 (2845) PA 6.6 & PA6I/6T Dry, 40% Glass Filled
- Albis Plastics Cellulose Acetate Butyrate B900 (Base Grade), 10% Plasticizer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved