SABIC Innovative Plastics LNP Thermocomp KB002 Acetal Copoly

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Glass Bead Filled
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp KB002 Acetal Copoly.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* KB002 is a compound based on Acetal Copolymer resin containing Glass Bead.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.48 g/cc
0.0535 lb/in³
ASTM D 792
Linear Mold Shrinkage, Flow 0.020 cm/cm

@Time 86400 sec
 0.020 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 48.0 MPa
6960 psi
ASTM D 638
Elongation at Break 8.4 %
8.4 %
ASTM D 638
Tensile Modulus 3.55 GPa
515 ksi
50 mm/min; ASTM D 638
Flexural Strength 75.0 MPa
10900 psi
ASTM D 790
Flexural Modulus 2.76 GPa
400 ksi
ASTM D 790
Izod Impact, Notched 0.370 J/cm

@Temperature 23.0 °C
 0.693 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 7.29 J/cm

@Temperature 23.0 °C
 13.7 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 101 °C

@Thickness 3.20 mm
 214 °F

@Thickness 0.126 in
 unannealed; ASTM D 648