Polykemi AB POLYform POM C M270 UV Polyoxymethylene
| Category | Polymer , Thermoplastic |
| Manufacturer | Polykemi AB |
| Trade Name | POLYform |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYform POM C M270 UV Polyoxymethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | With Flow; ISO 2577 |
| 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 27 g/10 min @Load 2.16 kg, Temperature 190 °C |
27 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 97 @Time 15.0 sec |
97 @Time 0.00417 hour |
D2240 |
| Hardness, Shore D | 78 @Time 15.0 sec |
78 @Time 0.00417 hour |
ASTM D2240 |
| Tensile Strength at Break | <= 60.0 MPa | <= 8700 psi | ISO/R527 |
| Elongation at Yield | 10 % | 10 % | ISO/R527 |
| Flexural Strength | <= 85.0 MPa | <= 12300 psi | ISO 178 |
| Flexural Modulus | 2.70 GPa @Temperature 23.0 °C |
392 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 |
| NB @Temperature -20.0 °C |
NB @Temperature -4.00 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -20.0 °C |
1.90 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C | 223 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 152 °C @Load 5.001 kg |
306 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 550 °C @Thickness 3.20 mm |
1020 °F @Thickness 0.126 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® BFL4000U PC (Europe-Africa-Middle East)
- Lehmann & Voss LUVOCOM® 19-7342 Polyamide 46, with carbon fiber
- Kolon SPESIN® KP213HIBL Impact Resistant PBT Compound resin
- Sylvin Technologies 8940-80 Natural PVC Extrusion Compound
- Wellman Wellamid® MR409 22H-NBK1 Nylon 66, 40% Mineral Reinforced
- DuPont Nucrel® 903 Ethylene-Methacrylic Acid Copolymer Resin for Blown and Cast Film
- DuPont Performance Polymers Zytel® FR50 NC010A Nylon 66 (Unverified Data**)
- Azoty Tarnow™ Tarnamid® T-27 GF10 MX6 Polyamide 6 - Flame Retarded, Reinforced
- Lucobit Lucobit® 1218 Ethylene Copolymer Bitumen
Copyright © lookpolymers.com All Rights Reserved