Chevron Phillips Marlex® HXM 50100-02 Extra high molecular weight hexene copolymer (discontinued **)

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), UHMW PE Ultra High Molecular Weight
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chevron Phillips Marlex® HXM 50100-02 Extra high molecular weight hexene copolymer (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Benefits: excellent balance of stress cracking resistance, good melt strength, excellent stress cracking resistance, good rigidity, excellent impact strength even at low temperaturesCharacteristics: Bottle ESCR > 700 h, 8-13 cm sheet sagApplications: 55-gallon shipping containers, gasoline tanks, agricultural chemical tanks, pallets, cattle feeders, large formed parts, boatsInformation provided by Chevron Phillips Chemical Company

Physical Properties	Metric	English	Comments
Density	0.950 g/cc	0.0343 lb/in³	ASTM D1505
Environmental Stress Crack Resistance	>= 600 hour @Temperature 50.0 °C	>= 600 hour @Temperature 122 °F	Condition A and Condition B; ASTM D 1693
High Load Melt Index	8.3 g/10 min @Load 21.6 kg, Temperature 190 °C	8.3 g/10 min @Load 47.6 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	25.0 MPa	3630 psi	ASTM D638 Type IV
Elongation at Break	>= 600 %	>= 600 %	ASTM D638 Type IV
Flexural Modulus	1.172 GPa	170.0 ksi	ASTM D790

Thermal Properties	Metric	English	Comments
Brittleness Temperature	<= -91.0 °C	<= -132 °F	ASTM D746

Processing Properties	Metric	English	Comments
Processing Temperature	154 - 182 °C	309 - 360 °F	Thermoforming Surface
	188 - 232 °C	370 - 450 °F	Blow Molding
	232 - 268 °C	450 - 514 °F	Extrusion