SABIC Innovative Plastics LNP Lubricomp RL001 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, PTFE Filled |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp RL001 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP Lubricomp* RL001 is a Nylon 6/6 base resin containing PTFE lubricant. Characteristics are internally lubricated.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| 1.17 g/cc | 0.0423 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 1.4 % | 1.4 % | 23°C / 50% RH; ISO 62 |
| 0.94 % @Time 86400 sec |
0.94 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 78.0 MPa | 11300 psi | 5 mm/min; ISO 527 |
| 80.0 MPa | 11600 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 78.0 MPa | 11300 psi | 5 mm/min; ISO 527 |
| 80.0 MPa | 11600 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 3.6 % | 3.6 % | 5 mm/min; ISO 527 |
| 3.7 % | 3.7 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 3.6 % | 3.6 % | 5 mm/min; ISO 527 |
| 3.7 % | 3.7 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 3.44 GPa | 499 ksi | 50 mm/min; ASTM D 638 |
| 3.73 GPa | 541 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 101 MPa | 14600 psi | ISO 178 |
| Flexural Modulus | 2.86 GPa | 415 ksi | 2 mm/min; ISO 178 |
| 2.94 GPa | 426 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.360 J/cm @Temperature 23.0 °C |
0.674 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 5.90 J/cm @Temperature 23.0 °C |
11.1 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 57.0 kJ/m² @Temperature 23.0 °C |
27.1 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 10.0 J | 7.38 ft-lb | Multiaxial Impact; ISO 6603 |
| 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 | |
| Coefficient of Friction, Dynamic | 0.50 | 0.50 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.39 | 0.39 | ASTM D 3702 Modified |
| K (wear) Factor | 359 x 10-8 mm³/N-M | 178 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 164 °C | 327 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 224 °C @Thickness 3.20 mm |
435 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 72.0 °C @Thickness 3.20 mm |
162 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Indium Corp. Indalloy 34 Bismuth Solder Alloy
- Solvay Chemicals Hydrofluoric acid
- SABIC Innovative Plastics LNP THERMOCOMP MX88028 PP (Asia Pacific)
- TIMET TIMETAL® 6-4 ELI Titanium Alloy (Ti-6Al-4V ELI; ASTM Grade 23) (Annealed; 2.50 - 4.00 in Rod or Thickness; Per ASTM F136)
- DuPont Teijin Films Melinex® ST505 Polyester Film, 700 Gauge
- 3M Controltac™ 162-114 Graphic Film
- American Elements Cobalt Iron Nanopowder
Copyright © lookpolymers.com All Rights Reserved