KKPC KOSYN KNB 230 Acrylonitrile Butadiene Rubber (NBR)

Category	Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE)
Manufacturer	Korea Kumho Petrochemical Co., Ltd.
Trade Name	KOSYN
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	KKPC KOSYN KNB 230 Acrylonitrile Butadiene Rubber (NBR).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Acrylonitrile Butadiene Rubber (NBR)Characteristics: KOSYN KNB is copolymer of high oil resistance and chemical resistance made from acrylonitrile and butadiene by the cold emulsion polymerization. Our NBR has superior working properties such as roll winding properties, compounding dispersibility and extrusion properties. Also, it is easily processed on account of the excellent vulcanization properties.Applications: General oil-resistant Rubber Products such as packing, gasket, hose, rolls, and shoe solesAdditional Notes: Bound Acrylonitrile: 35%Compound Properties: NBR 100, ZnO 3, Stearic Acid 1, HAF Black (IRB#7) 40, Accelerator TBBS 1, Sulfur 1.5, Total: 146.5Volume Change: 0%This product is so sensitive to sunlight and humidity that it can be tarnished and caused deterioration of quality if exposed. It is recommended to store it in cool and shady area lest it should be exposed to direct sunlight. Do not expose to incompatible materials or contaminants.Data provided by Korea Kumho Petrochemical Co., Ltd.

Physical Properties	Metric	English	Comments
Density	0.900 g/cc	0.0325 lb/inÂ³	Not Compounded
Mooney Viscosity	56 @Temperature 100 Â°C	56 @Temperature 212 Â°F	Raw; ML1+4
	60 @Temperature 100 Â°C	60 @Temperature 212 Â°F	Compounded; ML1+4

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	74	74	150Â°C, 40 min., Pressure Vulcanization. -1% Change after 100Â°C, 70 hrs, Oil Immersion
Tensile Strength, Ultimate	29.4 MPa	4270 psi	150Â°C, 40 min., Pressure Vulcanization. -3% Change after 100Â°C, 70 hrs, Oil Immersion
Elongation at Break	500 %	500 %	150Â°C, 40 min., Pressure Vulcanization. -25% Change after 100Â°C, 70 hrs, Oil Immersion
300% Modulus	0.0157 GPa	2.28 ksi	150Â°C, 40 min., Pressure Vulcanization. 40% Change after 100Â°C, 70 hrs, Oil Immersion

Thermal Properties	Metric	English	Comments
Shrinkage	0.000 % @Time 252000 sec	0.000 % @Time 70.0 hour	after Oil Immersion

Users viewing this material also viewed the following: