SABIC Innovative Plastics LNP Lubricomp OFG26XXP PPS - Linear

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp OFG26XXP PPS - Linear.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* OFG26XXP is a compound based on Linear PPS containing Glass Fiber and Graphite Powder. Characteristics of this grade are Internally Lubricated.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.67 g/cc
1.67 g/cc
ASTM D 792
Density 1.66 g/cc
0.0600 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.00 %
0.00 %
23°C / 50% RH; ISO 62
0.00 %

@Time 86400 sec
 0.00 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm

@Time 86400 sec
 0.0030 - 0.0050 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.0080 - 0.010 cm/cm

@Time 86400 sec
 0.0080 - 0.010 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 133 MPa
19300 psi
5 mm/min; ISO 527
140 MPa
20300 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 133 MPa
19300 psi
5 mm/min; ISO 527
141 MPa
20500 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 1.2 %
1.2 %
5 mm/min; ISO 527
1.4 %
1.4 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 1.2 %
1.2 %
5 mm/min; ISO 527
1.4 %
1.4 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 14.42 GPa
2091 ksi
1 mm/min; ISO 527
14.82 GPa
2149 ksi
50 mm/min; ASTM D 638
Flexural Strength 199 MPa
28900 psi
1.3 mm/min, 50 mm span; ASTM D 790
201 MPa
29200 psi
ISO 178
Flexural Modulus 13.4 GPa
1940 ksi
1.3 mm/min, 50 mm span; ASTM D 790
13.55 GPa
1965 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.570 J/cm

@Temperature 23.0 °C
 1.07 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 4.24 J/cm

@Temperature 23.0 °C
 7.94 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
 2.38 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 26.0 kJ/m²

@Temperature 23.0 °C
 12.4 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
7.00 J

@Temperature 23.0 °C
 5.16 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Coefficient of Friction, Dynamic 0.34
0.34
ASTM D 3702 Modified
Coefficient of Friction, Static 0.37
0.37
ASTM D 3702 Modified
K (wear) Factor 58.4 x 10-8 mm³/N-M
29.0 x 10-10 in³-min/ft-lb-hr
Ring; ASTM D 3702 Modified
252 x 10-8 mm³/N-M
125 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 22.1 µm/m-°C

@Temperature -30.0 - 30.0 °C
 12.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
CTE, linear, Transverse to Flow 42.3 µm/m-°C

@Temperature -30.0 - 30.0 °C
 23.5 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 275 °C
527 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
277 °C

@Thickness 3.20 mm
 531 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 258 °C
496 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
264 °C

@Thickness 3.20 mm
 507 °F

@Thickness 0.126 in
 unannealed; ASTM D 648