SABIC Innovative Plastics LNP Lubricomp KFL32L Acetal Copolymer (Asia Pacific)

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 10% Glass Fiber Reinforced , Acetal Copolymer, PTFE Filled
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP Lubricomp KFL32L Acetal Copolymer (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

LNP* Lubricomp* KFL32L is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.This data was supplied by SABIC-IP for the Asia Pacific region.

Physical Properties	Metric	English	Comments
Density	1.58 g/cc	0.0571 lb/inÂ³	ASTM D 792
Linear Mold Shrinkage, Flow	0.0060 cm/cm @Time 86400 sec	0.0060 in/in @Time 24.0 hour	ASTM D 955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	76.0 MPa	11000 psi	ASTM D 638
Elongation at Break	2.5 %	2.5 %	ASTM D 638
Tensile Modulus	5.51 GPa	799 ksi	50 mm/min; ASTM D 638
Flexural Strength	110 MPa	16000 psi	ASTM D 790
Flexural Modulus	4.72 GPa	685 ksi	ASTM D 790
Izod Impact, Notched	0.530 J/cm @Temperature 23.0 Â°C	0.993 ft-lb/in @Temperature 73.4 Â°F	ASTM D 256
Izod Impact, Unnotched	5.03 J/cm @Temperature 23.0 Â°C	9.42 ft-lb/in @Temperature 73.4 Â°F	ASTM D 4812

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	161 Â°C @Thickness 3.20 mm	322 Â°F @Thickness 0.126 in	unannealed; ASTM D 648