DuPont Performance Polymers GBL-200 Formulation (discontinued **)
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers GBL-200 Formulation
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FormulationViton® GBL-200
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 26 @Temperature 121 °C |
26 @Temperature 250 °F |
ML-10 (gum) |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 71 | 71 | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Elongation at Break | 230 % | 230 % | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Modulus of Elasticity | 0.000700 GPa | 0.102 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| 100% Modulus | 0.00530 GPa | 0.769 ksi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Compression Set | 32 % @Temperature 200 °C |
32 % @Temperature 392 °F |
Method B, O-rings 22 hr at 200°C (Post Cured 16 hr at 232°C) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | -17.9 °C | -0.220 °F | DSC, modulated, midpoint |
Users viewing this material also viewed the following:
- Nyco M1250 AS WOLLASTOCOAT® Wollastonite
- S&E Specialty Polymers GM-3950-095 PVC
- Polykemi AB POLYelast TPE Z800 SHF Thermoplastic Elastomer, SEBS-based
- Overview of materials for High Density Polyethylene (HDPE), Carbon Black Filled
- Taiwan PU Corporation TPUI-G98 High Wear Resistance, Injection Molding Polycaprolactone Base TPU
- SABIC Innovative Plastics ULTEM AUT230 PEI (Asia Pacific)
- Clariant Renol PA213G50 Nylon 6, 50% Glass Fiber, Heat Stabilized, Lubricated
- BASF Ultramid® KR 4365 G5 35% Glass Filled PA6/6T FR (Dry)
- Solvay Specialty Polymers Algoflon® L100 Polytetrafluoroethylene (PTFE) (Unverified Data**)
- DSM Stanyl® TC502 PA46
Copyright © lookpolymers.com All Rights Reserved