PolyOne Bergadur™ PB40 G30 UF UV Polybutylene Terephthalate (PBT)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | PolyOne Corporation |
| Trade Name | Bergadur™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Bergadur™ PB40 G30 UF UV Polybutylene Terephthalate (PBT).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ±0.03 g/cm³; DIN 53479 |
| Melt Index of Compound | 14 g/10 min @Load 1.60 kg, Temperature 250 °C |
14 g/10 min @Load 3.53 lb, Temperature 482 °F |
cm³/10min; ISO 1133 |
| Ash | 30 % | 30 % | ISO 3451 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 MPa @Temperature 23.0 °C |
13100 psi @Temperature 73.4 °F |
ISO 527-2/5 |
| Elongation at Break | 2.5 % @Temperature 23.0 °C |
2.5 % @Temperature 73.4 °F |
ISO 527-2/5 |
| Tensile Modulus | 8.20 GPa @Temperature 23.0 °C |
1190 ksi @Temperature 73.4 °F |
ISO 527-2/1 |
| Charpy Impact Unnotched | 7.40 J/cm² @Temperature 23.0 °C |
35.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 224 °C | 435 °F | ISO 3146 |
| Maximum Service Temperature, Air | 140 °C | 284 °F | Continuous (GTP 50% Tensile); IEC 60216 |
| 170 °C | 338 °F | Short Time; IEC 60216 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | Unannealed; ISO 75-2/B |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
Internal Method |
| Glow Wire Test | 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
Ignition Temperature; IEC 60695-2-13 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | UV Stabilizer | |
| Features | Flame Retardant | |
| Halogen Free | ||
| Low (to None) Phosphorus Content | ||
| Filler / Reinforcement | Glass Fiber Reinforcement, 30% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | PBT | |
| Generic Name | Polybutylene Terephthalate (PBT) | |
| Regional Availability | Africa & Middle East | |
| Europe | ||
| RoHS Compliance | RoHS Compliant |
Users viewing this material also viewed the following:
- Parker Chomerics Tecknit Teckfip™ FIP-A Formed in Place Conductive Elastomer
- NIZHNEKAMSKNEFTEKHIM PE 4436S (35405) Medium Density Polyethylene
- LG Chemical LUPOY GP5008A PC/ABS
- H.C. Starck Amperit® 155.086 Titanium (Ti)
- Lucobit Lucowax® 1700 Polyethylene Wax
- Samsung Cheil Industries Starex® WX-9300UV ASA, Unreinforced Heat Resistant
- SK Chemicals SKYTHANE® UB420 Hotmelt Lamination Film
- A. Schulman POLYFORT™ FPP 1697HU High Flow Fortified Polypropylene
- Cossa Polimeri ESTAPROP H 1080 TG Polypropylene, 40% Mineral Filled
Copyright © lookpolymers.com All Rights Reserved