Lubrizol Pellethane® 2363-80AE Thermoplastic Polyurethane Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | Pellethane® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Pellethane® 2363-80AE Thermoplastic Polyurethane Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: USP Class VIAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product line from Dow in 2009.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm @Thickness 1.59 mm |
0.0050 - 0.0080 in/in @Thickness 0.0625 in |
plaque |
| Linear Mold Shrinkage, Transverse | -0.00100 - 0.0040 cm/cm @Thickness 1.59 mm |
-0.00100 - 0.0040 in/in @Thickness 0.0625 in |
plaque |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 224 °C |
10 g/10 min @Load 4.76 lb, Temperature 435 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 81 - 89 | 81 - 89 | ASTM D2240 |
| Tensile Strength, Ultimate | 28.9 MPa | 4190 psi | ASTM D412 |
| Elongation at Break | 550 % | 550 % | ASTM D412 |
| 50% Modulus | 0.00480 GPa | 0.696 ksi | ASTM D412 |
| 100% Modulus | 0.00610 GPa | 0.885 ksi | ASTM D412 |
| 300% Modulus | 0.0103 GPa | 1.49 ksi | ASTM D412 |
| Tear Strength | 73.6 kN/m | 420 pli | Die C; ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 30 | 30 | H22 Wheel, 1000g; ASTM D1044 |
| Compression Set | 30 % @Temperature 25.0 °C, Time 79200 sec |
30 % @Temperature 77.0 °F, Time 22.0 hour |
ASTM D395 Method B |
| 80 % @Temperature 70.0 °C, Time 79200 sec |
80 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395 Method B | |
| Tensile Set | 70 % | 70 % | Elongation set after break; ASTM D412 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 165 µm/m-°C @Temperature 20.0 °C |
91.7 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Vicat Softening Point | 81.7 °C | 179 °F | ASTM D1525 |
| Glass Transition Temp, Tg | -47.0 °C | -52.6 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 190 - 205 °C | 374 - 401 °F | Molding |
| 190 - 205 °C | 374 - 401 °F | Extrusion | |
| Mold Temperature | 15.0 - 60.0 °C | 59.0 - 140 °F | |
| Drying Temperature | 80.0 - 95.0 °C | 176 - 203 °F |
Users viewing this material also viewed the following:
- Osprey Metals Fe3Si Binary Alloy Powder (Grade 95% - 16)
- Lotte Chemical Titan TITANCEED® mL1064 Linear low density polyethylene resin (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-7506 PEEK, with carbon fiber
- Kingfa JH950-602 Low-temperature Resistant & Flame Retardant PC/ABS Alloy
- Gwent Electronic Materials C2080409D2 Silver/Silver Chloride Paste
- KaMin KaMin® Tek 2001 Clay
- Dynasol Calprene® 710 Thermoplastic Rubber SBS Dry
- PolyOne Edgetek® AM-20CF-20GF/000 Polyphthalamide (PPA), Glass/Carbon Fiber Filled (discontinued **)
- DuPont Performance Polymers Rynite® 940 BK505 PET (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved