SABIC Innovative Plastics LNP LUBRILOY RF203 PA 66 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRILOY RF203 PA 66 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRILOY* RF203 is a compound based on PA 66 resin containing Glass Fiber, Proprietary Lubricant. Added features include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Water Absorption | 0.37 % @Time 86400 sec |
0.37 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 99.0 MPa | 14400 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.5 % | 3.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 5.30 GPa | 769 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 122 MPa | 17700 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 133 MPa | 19300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.10 GPa | 595 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.36 | 0.36 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.30 | 0.30 | ASTM D3702 Modified |
| K (wear) Factor | 141 x 10-8 mm³/N-M | 70.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 41.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
22.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 131 µm/m-°C @Temperature 23.0 - 60.0 °C |
72.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Parker Chomerics Tecknit SC-Consil® 862 Carbon-Filled Silicone Elastomer
- Kinlead PT12 Adhesive Tape Grade BOPP Plain Film (thickness: 28 µm)
- Greene Tweed CHEMRAZ® 505 Perfluoroelastomer
- Sharadaa Ceramics REFCAST Dense Castables
- Samyang Trirex® 3500G30 Polycarbonate, 30% Glass Reinforced
- Addcomp ADD-VANCE® THC 732 PP based masterbatch containing heat stabilizers, coupling agent and carbon black
- Barlog Plastics KEBAFLEX E 90.1 TPE-V, Shore A90
Copyright © lookpolymers.com All Rights Reserved