| Category | Polymer , Thermoplastic , AES Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRILOY Lexan_WR6300 AES+PC+SAN.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubriloy* Lexan_WR6300 compound is a wear resistant PC+SAN, with proprietary lubricant, for business equipment applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound | 38 g/10 min @Load 2.16 kg, Temperature 300 °C |
38 g/10 min @Load 4.76 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 164 % | 164 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 96.0 MPa | 13900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.48 GPa | 360 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 6.78 J/cm | 12.7 ft-lb/in | ASTM D256 |
| 1.65 J/cm @Temperature -30.0 °C |
3.09 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 25.31 J/cm | 47.42 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 60.0 J @Temperature 23.0 °C |
44.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 106 µm/m-°C @Temperature -40.0 - 40.0 °C |
58.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 119 µm/m-°C @Temperature -40.0 - 40.0 °C |
66.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 133 °C @Thickness 6.40 mm |
271 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 117 °C @Thickness 3.20 mm |
243 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 121 °C @Thickness 6.40 mm |
250 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 136 °C | 277 °F | Rate B/50; ASTM D1525 |
| UL RTI, Electrical | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.49 mm |
HB @Thickness 0.0587 in |
UL 94 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible XV 3450 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Materion Nibryl Beryllium Nickel Alloy (Nibryl)-360 Rod and Bar; H925 (H925) Temper; All Sizes (UNS N03360)
- Johnson Matthey SW 850 Platinum w/ 15% Iridium Jewelry Alloy
- Lehmann & Voss LUVOCOM® 1105-0904/GN PEEK, with glass fiber
- SABIC Innovative Plastics LNP THERMOCOMP QF00A PA6.10
- CMW® ELKONITE® 30W3 Infiltrated Copper Tungsten contact material ASTM B702, Class E, infiltrated, RWMA Class 12
- Colorite Polymers 8511G-015 (Extrustion), 8512G-015 (Molding) Radiation Sterilizable Vinyl Compound
- Beijing Ranger Chem SM-828L Liquid Epoxy Resin
- Goodfellow Audiolloy® Iron 52/Nickel 48 Alloy
Copyright © lookpolymers.com All Rights Reserved