SABIC Innovative Plastics LNP LUBRICOMP WL004 PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP WL004 PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* WL004 is a compound based on Polybutylene Terephalate resin containing PTFE.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.010 - 0.017 cm/cm | 0.010 - 0.017 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.017 cm/cm | 0.0080 - 0.017 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 12.2 % | 12.2 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 2.40 GPa | 348 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 67.0 MPa | 9720 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.32 | 0.32 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.25 | 0.25 | ASTM D3702 Modified |
| K (wear) Factor | 117 x 10-8 mm³/N-M | 58.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 117 µm/m-°C @Temperature 23.0 - 60.0 °C |
65.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 107 µm/m-°C @Temperature 23.0 - 60.0 °C |
59.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Polymer Resources PC-FR3-D Polycarbonate, Improved Flame Retardant, High Flow
- SABIC Innovative Plastics SABIC PPCOMPOUND 9712 PP
- Solvay Chemicals Hydrogen fluoride
- Universal Wire Works 4643 (AMS 4189) Aluminum Alloy Filler Metal
- Tisan TISESTER® Flame Retardant (V0). Heat Stabilized Polybutylene Terephthalate
- Total PPH 3371 Polypropylene, Oriented Film Extrusion Grade
- Dow ISONATE™ 181 MDI Prepolymer
- Asahi Glass Lumiflon LF-910LM Solvent Soluble Fluoropolymer
- Albis Plastics Cellulose Acetate Butyrate B900 (Base Grade), 10% Plasticizer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved