BASF Ultramid® A3EG7 BK00564 35% Glass Filled PA66 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® A3EG7 BK00564 35% Glass Filled PA66 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid A3EG6 BK00564 is a 35% glass fiber reinforced injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| Water Absorption | 1.6 % | 1.6 % | 24 hour; ISO Test |
| 5.0 % | 5.0 % | ISO 62 | |
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 23°C/50% R.H.; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 190 MPa | 27600 psi | 5mm/min; ISO 527 |
| Elongation at Break | 2.8 % | 2.8 % | 5mm/min; ISO 527 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ISO Data |
| Izod Impact, Notched (ISO) | 9.50 kJ/m² | 4.52 ft-lb/in² | ISO Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | 10 K/min |
| 260 °C | 500 °F | ASTM Test | |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK00564 | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Polymer Resources PPX-FR1-[color]-EN Modified-PPO, V-0 Flame Retardant, Extrusion Grade
- Techmer ES Electrafil® J-50/CF/10/TF/13/SI/2 Polycarbonate, 10% Carbon Fiber Reinforced, 13% PTFE, 2% Silicone
- SSAB Tunnplat Dogal 180 RP-X High-strength Metal-coated Steel
- Tisan TISOPLEN® 10% Talc Filled Heat Stabilized Copolymer Polypropylene
- Toyobo Vylopet® EMC330K Glass Reinforced Polyester, Easy Molding Grade
- Zylog Hipolyene® 4511 RM Thermoplastic Polyolefin & PP Compound
- ExxonMobil Jayflex™ DIDP Plasticizer (European Grade)
- Fainplast Compounds HL 100/2 Flexible PVC, Insulation for High Temperatures
- Dow DNDB-7441 NT 7 Linear Low Density Polyethylene Resin
- Azdel SuperLite® SL551800-100 PP Resin Matrix / 55% Glass Fiber (10 mm Molded Thickness)
Copyright © lookpolymers.com All Rights Reserved