SABIC Innovative Plastics LNP LUBRICOMP UL002S PPA
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP UL002S PPA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* UL002S is a compound based on Polyphthalamide resin containing 10% PTFE. Added features of this grade include: Heat Stabilized, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 |
| 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.470 % | 0.470 % | 50% RH, 24 hrs; ASTM D570 |
| 0.730 % | 0.730 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.020 cm/cm @Time 86400 sec |
0.0090 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | Type I, 5 mm/min; ASTM D638 |
| 60.0 MPa | 8700 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 58.0 MPa | 8410 psi | 5 mm/min; ISO 527 |
| 60.0 MPa | 8700 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.2 % | 2.2 % | Type I, 5 mm/min; ASTM D638 |
| 2.2 % | 2.2 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.1 % | 2.1 % | 5 mm/min; ISO 527 |
| 2.2 % | 2.2 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 3.17 GPa | 460 ksi | 50 mm/min; ASTM D638 |
| 3.21 GPa | 466 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 105 MPa | 15200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 105 MPa | 15200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.98 GPa | 432 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.260 J/cm | 0.487 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.53 J/cm | 8.49 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 27.0 kJ/m² | 12.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 2.00 J @Temperature 23.0 °C |
1.48 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.26 | 0.26 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.16 | 0.16 | ASTM D3702 Modified |
| K (wear) Factor | 40.3 x 10-8 mm³/N-M | 20.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® ML3041 PC (Europe-Africa-Middle East)
- Hexion Bakelite™ PF 31.9 Phenolic Formaldehyde Resin, Ammonia Free (discontinued **)
- Solvay TECHNYL® B 50 H1 PA66/6, DRY
- Techmer ES Elastoblend® PA6/6 GF33 IM HS L 33% Glass Filled
- Chase Plastics CP Pryme® A100HF ABS
- ExxonMobil EXXELOR™ PO 1020 Maleic anhydride functionalized polypropylene
- DuPont Performance Polymers Zytel® LC6601 NC010 Nylon 612
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 350ºF Cure Temperature
- Buckeye Polymers BP RPP 2520 CU Polypropylene, 25% Mineral Filled
Copyright © lookpolymers.com All Rights Reserved