SABIC Innovative Plastics LNP LUBRICOMP RX99518 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RX99518 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RX99518 is a compound based on PA66 containing Proprietary Fillers. Added feature of this material is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.760 % | 0.760 % | 50% RH, 24 hrs; ASTM D570 |
| 1.00 % | 1.00 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 5 mm/min; ISO 527 |
| 72.0 MPa | 10400 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 71.0 MPa | 10300 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 9.3 % | 9.3 % | 5 mm/min; ISO 527 |
| 9.4 % | 9.4 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 9.2 % | 9.2 % | Type I, 5 mm/min; ASTM D638 |
| 9.2 % | 9.2 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.14 GPa | 455 ksi | 5 mm/min; ASTM D638 |
| 3.18 GPa | 461 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 103 MPa | 14900 psi | ISO 178 |
| Flexural Modulus | 2.82 GPa | 409 ksi | 2 mm/min; ISO 178 |
| 2.88 GPa | 418 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.500 J/cm | 0.937 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.67 J/cm | 18.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 58.0 kJ/m² | 27.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 3.00 J @Temperature 23.0 °C |
2.21 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.37 | 0.37 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.35 | 0.35 | ASTM D3702 Modified |
| K (wear) Factor | 4.03 x 10-8 mm³/N-M | 2.00 x 10-10 in³-min/ft-lb-hr | Ring; ASTM D3702 Modified |
| 30.2 x 10-8 mm³/N-M | 15.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 8.50 µm/m-°C @Temperature -30.0 - 30.0 °C |
4.72 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 9.20 µm/m-°C @Temperature -30.0 - 30.0 °C |
5.11 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 181 °C | 358 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 216 °C @Thickness 3.20 mm |
421 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.0 °C | 163 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 95.0 °C @Thickness 3.20 mm |
203 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Plastcom PLASTAMID® 6HM PA6
- SABIC Innovative Plastics Cycoloy® FXC630SK PC+ABS
- S&E Specialty Polymers TufTech™ GM-93-060LT PVC Compound
- Ineos T50-500-171 Polyethylene Copolymer
- ExxonMobil 629 Mobil SHC 600 Series
- Tra-Con Tra-Bond 216H01 Blush-Free Non-Sag Structural Epoxy Adhesive
- Dow Corning LSPBK 22 SILICONE MASTERBATCH
- Arkema Group Pebax® 7033 SA 01 Polyether Block Amide (PEBA)
- BASF Butane-2,3-diol
Copyright © lookpolymers.com All Rights Reserved