SABIC Innovative Plastics LNP LUBRICOMP RX05050 PA 66 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RX05050 PA 66 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* RX05050 is a compound based on Nylon 66 resin containing PTFE, Aramid Fiber, Carbon Fiber. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0090 cm/cm | 0.0050 - 0.0090 in/in | on Tensile Bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 129 MPa | 18700 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.3 % | 3.3 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 8.70 GPa | 1260 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 187 MPa | 27100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.20 GPa | 1040 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
13.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 88.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
48.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C | 496 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1000 ohm - 1e+05 | 1000 ohm - 1e+05 | ASTM D257 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL1860T PC Copolymer (Europe-Africa-Middle East)
- SABIC Innovative Plastics ULTEM Foam XP080 PEI
- Shandong Rike Chemical HELIâ„¢ HL-400 PVC Foaming Regulator
- Diamond Polymers ABS 2100 P Compounding Grade Powder
- Epoxy Technology EPO-TEK® OG178 UV Cure Optical Epoxy
- Dow DMDA-8940 NT 7 High Density Polyethylene Resin
- Clariant Renol BR2025 Nylon 66, Impact Modified
- DSM Arnite® TV6 260 T PBT-I-GF30
- PolyOne Edgetek® AM-20CF/000 Polyphthalamide (PPA), Carbon Fiber Reinforced (discontinued **)
Copyright © lookpolymers.com All Rights Reserved