SABIC Innovative Plastics LNP LUBRICOMP RL0019 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RL0019 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* RL0019 is a compound based on Nylon 66 resin containing 5% PTFE. Added features of this material include: Flame Retardant, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ASTM D792 |
| 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.460 % | 0.460 % | 50% RH, 24 hrs; ASTM D570 |
| 0.700 % | 0.700 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0189 cm/cm @Time 86400 sec |
0.0189 in/in @Time 24.0 hour |
ISO 294 |
| 0.019 cm/cm @Time 86400 sec |
0.019 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0196 cm/cm @Time 86400 sec |
0.0196 in/in @Time 24.0 hour |
ISO 294 |
| 0.020 cm/cm @Time 86400 sec |
0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 62.0 MPa | 8990 psi | ISO 527 |
| 68.0 MPa | 9860 psi | ASTM D638 | |
| Elongation at Break | 2.2 % | 2.2 % | ISO 527 |
| 2.8 % | 2.8 % | ASTM D638 | |
| Tensile Modulus | 3.41 GPa | 495 ksi | 50 mm/min; ASTM D638 |
| 3.64 GPa | 528 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 103 MPa | 14900 psi | ISO 178 |
| 109 MPa | 15800 psi | ASTM D790 | |
| Flexural Modulus | 3.27 GPa | 474 ksi | ISO 178 |
| 3.44 GPa | 499 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.210 J/cm | 0.393 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.31 J/cm | 6.20 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 1.00 J | 0.738 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 66.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 66.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 70.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 70.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 105 °C @Thickness 3.20 mm |
221 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ PPC-40T Nat Polypropylene Copolymer (PP Copolymer)
- Quadrant EPP Nylatron® GSM PA 6 + MoS2, cast (ISO Data)
- Radici Radilon® ALX14080 (dry) Nylon 66
- Ravago Manufacturing Americas Hylon® N1035HHR Nylon 6/6, 35% Fiberglass (DAM) (discontinued **)
- Heraeus Cleviosâ„¢ P Jet (OLED) Conductive Sulfonate Polymer for Antistatic Coatings
- Master Bond EP30ANHT Two Part, Electrically Isolating Epoxy Adhesive
- ChevronTexaco Havoline® SAE 5W-40 Synthetic Motor Oil
- Sumitomo Bakelite North America Epiall® 1961B-1 Mineral and Glass Filled Electrical Encapsulation Grade Epoxy
Copyright © lookpolymers.com All Rights Reserved