NCMT NanoPAC™ G1000 High Performance Polypropylene Nanocomposite
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Nano Composite Materials Technology Ltd |
| Trade Name | NanoPAC™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NCMT NanoPAC™ G1000 High Performance Polypropylene Nanocomposite.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Construction MaterialInformation provided by Nano Composite Materials Technology Limited
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | NCMT Method |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ASTM D638 |
| Izod Impact, Notched | 0.350 J/cm | 0.656 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 150 °C | 302 °F | Deflection Temp.; ASTM D648 |
Users viewing this material also viewed the following:
- NOVA Chemicals EPS 35MB Modified Expandable Polystyrene
- Iran Petrochemical (PCC) EP2C 37 F Polypropylene
- LATI Latamid 66 H2 G/25-V0KB PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
- Techmer ES HiFill® PA6 GF13 L 13% Glass Filled
- Polyplastics Duranex® 2002U Polybutylene Terephthalate (PBT), Weather resistance
- Tra-Con Tra-Bond 724-14C Polyurethane Adhesive
- A. Schulman POLYBATCH™ White LL8000 AP Concentrate Based In LLDPE
- CP-Polymer-Technik Wellamid® 6000 GS 20 HWCP 20% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry
- Unipetrol N - Butanol Synthetic
Copyright © lookpolymers.com All Rights Reserved