SABIC Innovative Plastics LNP LUBRICOMP RFL36XXZ PA 66 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RFL36XXZ PA 66 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP Lubricomp is a compound based on PA66 resin containing glass fiber, PTFE. It is an internally lubricated compound that provide excellent chemical resistance, strength and wear/friction properties. Also known as Lubricomp RFL-4036
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ASTM D792 |
| 1.51 g/cc | 0.0546 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.620 % | 0.620 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 138 MPa | 20000 psi | 5 mm/min; ISO 527 |
| 139 MPa | 20200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 |
| 2.1 % | 2.1 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 9.80 GPa | 1420 ksi | 1 mm/min; ISO 527 |
| 11.23 GPa | 1629 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 236 MPa | 34200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 211 MPa | 30600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 9.70 GPa | 1410 ksi | 2 mm/min; ISO 178 |
| 9.75 GPa | 1410 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.06 J/cm | 1.99 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.07 J/cm | 17.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 51.0 kJ/m² | 24.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.58 | 0.58 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.49 | 0.49 | ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 37.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 37.8 µm/m-°C @Temperature 23.0 - 60.0 °C |
21.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 55.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
30.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| 55.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 248 °C @Thickness 3.20 mm |
478 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Veradel® 3200 Polyethersulfone (PESU) (Unverified Data**)
- Overview of materials for Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled
- DuPont Performance Polymers Zytel® 70G35HSL BK039B Nylon 66 (Unverified Data**)
- Lubriplate SFL-2 Aluminum Complex Synthetic Food Machinery Grade Grease
- Supreme Petrochem SP 6503 High Impact Polystyrene
- Teknor Apex Telcar® OBC 2581B Thermoplastic Elastomer
- Westlake Plastics Tempalux® 5000 Polyetherimide
- ArcelorMittal Save 25-16 Electrical Steel
- ExxonMobil Santoprene® 253-50W232 Thermoplastic Vulcanizate (discontinued **)
Copyright © lookpolymers.com All Rights Reserved