LATI Latigray 37 B01-01 CX/35 Bio-Polymer

Category	Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer
Manufacturer	LATI
Trade Name	Latigray
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latigray 37 B01-01 CX/35 Bio-Polymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Radiopaque compound based on Bio-Polymer (PLA, PHB, ...). Special mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.80 g/cc	0.0650 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0015 - 0.0040 cm/cm	0.0015 - 0.0040 in/in
Linear Mold Shrinkage, Transverse	0.0015 - 0.0040 cm/cm	0.0015 - 0.0040 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	35.0 MPa	5080 psi
Elongation at Break	3.5 %	3.5 %
Tensile Modulus	8.80 GPa	1280 ksi
Charpy Impact Unnotched	1.20 J/cmÂ²	5.71 ft-lb/inÂ²
Charpy Impact, Notched	0.180 J/cmÂ²	0.857 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	55.0 Â°C	131 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	50.0 Â°C	122 Â°F
Vicat Softening Point	60.0 Â°C @Load 5.00 kg	140 Â°F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	180 - 200 Â°C	356 - 392 Â°F
Mold Temperature	15.0 - 30.0 Â°C	59.0 - 86.0 Â°F
Drying Temperature	40.0 - 50.0 Â°C @Time 21600 sec	104 - 122 Â°F @Time 6.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa