SABIC Innovative Plastics LNP LUBRICOMP QP004 PA 6/10
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP QP004 PA 6/10.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* QP004 is a compound based on Nylon 6/10 containing 20% PTFE/Silicone. Added feature of this grade is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.330 % | 0.330 % | 50% RH, 24 hrs; ASTM D570 |
| 0.510 % | 0.510 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.040 cm/cm @Time 86400 sec |
0.010 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 |
| 48.0 MPa | 6960 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | Type I, 5 mm/min; ASTM D638 |
| 48.0 MPa | 6960 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 9.2 % | 9.2 % | 5 mm/min; ISO 527 |
| 10.9 % | 10.9 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 9.0 % | 9.0 % | 5 mm/min; ISO 527 |
| 10.5 % | 10.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.17 GPa | 315 ksi | 1 mm/min; ISO 527 |
| 2.23 GPa | 323 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 69.0 MPa | 10000 psi | ISO 178 |
| Flexural Modulus | 1.99 GPa | 289 ksi | 2 mm/min; ISO 178 |
| 2.04 GPa | 296 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.290 J/cm | 0.543 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.14 J/cm | 7.76 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 3.00 J @Temperature 23.0 °C |
2.21 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.26 | 0.26 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.10 | 0.10 | ASTM D3702 Modified |
| K (wear) Factor | 8.06 x 10-8 mm³/N-M | 4.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 113 µm/m-°C @Temperature -30.0 - 30.0 °C |
62.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 108 µm/m-°C @Temperature -30.0 - 30.0 °C |
60.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 170 °C @Thickness 3.20 mm |
338 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 57.0 °C @Thickness 3.20 mm |
135 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Overview of materials for Thermoplastic Olefinic Elastomer (TPO)
- Michelman® CleanGrip® 111 Alumina based, nonskid coating
- Indium Corp. Germanium Corporation® Germanium Metal
- SABIC Innovative Plastics LNP Thermocomp AF0029 ABS
- Sax Polymers SAXLAC 320U Acrylonitrile Butadiene Styrene
- Schmolz + Bickenbach UGICHROM 4418 Martensitic Chrome Plated Bar
- Teknor Apex Telcar® TL-1996F Thermoplastic Elastomer
- Eagle Brass 770 Nickel Silver 18%, Extra Spring
- Trelleborg Commercial Neoprene® C803 Chloroprene
Copyright © lookpolymers.com All Rights Reserved