SABIC Innovative Plastics LNP LUBRICOMP OFL36A PPS (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP OFL36A PPS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* OFL36A is a compound based on Polyphenylene Sulfide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.69 g/cc
0.0611 lb/in³
ASTM D792
1.69 g/cc
0.0611 lb/in³
ISO 1183
Moisture Absorption 0.0400 %
0.0400 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0010 - 0.0020 cm/cm

@Time 86400 sec
 0.0010 - 0.0020 in/in

@Time 24.0 hour
 ASTM D955
0.0013 - 0.0018 cm/cm

@Time 86400 sec
 0.0013 - 0.0018 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.0030 - 0.0048 cm/cm

@Time 86400 sec
 0.0030 - 0.0048 in/in

@Time 24.0 hour
 ISO 294
0.0030 - 0.0050 cm/cm

@Time 86400 sec
 0.0030 - 0.0050 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 124 MPa
18000 psi
ISO 527
144 MPa
20900 psi
ASTM D638
Elongation at Break 1.4 %
1.4 %
ISO 527
1.7 %
1.7 %
ASTM D638
Tensile Modulus 11.1 GPa
1610 ksi
1 mm/min; ISO 527
12.34 GPa
1790 ksi
50 mm/min; ASTM D638
Flexural Strength 197 MPa
28600 psi
ISO 178
199 MPa
28900 psi
ASTM D790
Flexural Modulus 10.95 GPa
1588 ksi
ISO 178
11.03 GPa
1600 ksi
ASTM D790
Izod Impact, Notched 0.850 J/cm
1.59 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.50 J/cm
10.3 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 26.0 kJ/m²
12.4 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 3.00 J
2.21 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.44
0.44
ASTM D3702 Modified
Coefficient of Friction, Static 0.35
0.35
ASTM D3702 Modified
K (wear) Factor 66.5 x 10-8 mm³/N-M
33.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 23.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 13.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
23.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 13.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 48.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 27.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
50.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
 27.8 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 266 °C
511 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
268 °C

@Thickness 3.20 mm
 514 °F

@Thickness 0.126 in
 unannealed; ASTM D648