SABIC Innovative Plastics LNP LUBRICOMP OCL36A PPS - Branched (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP OCL36A PPS - Branched (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* OCL4036 is a compound based on PPS - Branched resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ISO 1183 |
| Melt Index of Compound | 5.0 g/10 min @Load 5.00 kg, Temperature 315 °C |
5.0 g/10 min @Load 11.0 lb, Temperature 599 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 153 MPa | 22200 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 0.70 % | 0.70 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 25.0 GPa | 3630 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 217 MPa | 31500 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 21.3 GPa | 3090 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 3.00 µm/m-°C @Temperature 23.0 - 60.0 °C |
1.67 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 49.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
27.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 278 °C | 532 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 1.80 mm |
V-0 @Thickness 0.0709 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10 - 1000 ohm | 10 - 1000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Parker Chomerics CHOFORM® 5550 Conductive Form-in-Place Gasket
- Polymer Resources PC/TP-GP2-G20 PC/Polyester Alloy, 20% Glass Reinforced
- LG Chemical LUMID GP2339B(W) PA66+GF33%, General Purpose
- Materion Brush 1915â„¢ Hard Temper Rod, 0.050" - 0.375"
- Greene Tweed CHEMRAZ® 615 Perfluoroelastomer
- MTI ThermoStran® PA66-30C Long Carbon Fiber Compound
- Techmer ES HiFill® PA6 GF33 L UV 33% Glass Filled
- Suzhou Hipro Polymers Hiprolon® 90 NN Nylon 612, dry
- Eagle Brass 194 HSM® Copper, Extra Spring
- Fainplast Compounds GS 7303 Flexible PVC, Injection Molding for Footwear
Copyright © lookpolymers.com All Rights Reserved