DuPont Performance Polymers Crastin® SK605 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF DuPont Performance Polymers Crastin® SK605 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
30% Glass Reinforced Polybutylene Terephthalate Crastin SK605 NC010 is a 30% glass fiber reinforced lubricated polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
1.53 g/cc
0.0553 lb/in³
ISO 1183
Water Absorption 0.35 %
<br>@Thickness 2.00 mm
 0.35 %
<br>@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.150 %
<br>@Thickness 2.00 mm
 0.150 %
<br>@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 91150 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 260 °C
 91150 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 500 °F
 ISO 11403-1 -2
107900 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 250 °C
 107900 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 482 °F
 ISO 11403-1 -2
129480 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 240 °C
 129480 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 464 °F
 ISO 11403-1 -2
274700 cP
<br>@Shear Rate 500 1/s,<br> Temperature 260 °C
 274700 cP
<br>@Shear Rate 500 1/s,<br> Temperature 500 °F
 ISO 11403-1 -2
340700 cP
<br>@Shear Rate 500 1/s,<br> Temperature 250 °C
 340700 cP
<br>@Shear Rate 500 1/s,<br> Temperature 482 °F
 ISO 11403-1 -2
424600 cP
<br>@Shear Rate 500 1/s,<br> Temperature 240 °C
 424600 cP
<br>@Shear Rate 500 1/s,<br> Temperature 464 °F
 ISO 11403-1 -2
Viscosity Test 100 cm³/g
100 cm³/g
ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
ISO 294-4 2577
Melt Flow 10 g/10 min
10 g/10 min
ISO 1133
7.0 g/10 min
<br>@Load 2.16 kg,<br> Temperature 250 °C
 7.0 g/10 min
<br>@Load 4.76 lb,<br> Temperature 482 °F
 cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 140 MPa
20300 psi
ISO 527-1/-2
Tensile Stress 8.08 MPa
<br>@Strain 0.250 %,<br> Temperature 160 °C
 1170 psi
<br>@Strain 0.250 %,<br> Temperature 320 °F
 ISO 11403-1 -2
22.5 MPa
<br>@Strain 0.250 %,<br> Temperature 40.0 °C
 3260 psi
<br>@Strain 0.250 %,<br> Temperature 104 °F
 ISO 11403-1 -2
24.9 MPa
<br>@Strain 0.250 %,<br> Temperature 23.0 °C
 3610 psi
<br>@Strain 0.250 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
28.9 MPa
<br>@Strain 0.250 %,<br> Temperature 0.000 °C
 4190 psi
<br>@Strain 0.250 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
30.0 MPa
<br>@Strain 0.250 %,<br> Temperature -20.0 °C
 4350 psi
<br>@Strain 0.250 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
30.7 MPa
<br>@Strain 0.250 %,<br> Temperature -40.0 °C
 4450 psi
<br>@Strain 0.250 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
30.7 MPa
<br>@Strain 1.50 %,<br> Temperature 160 °C
 4450 psi
<br>@Strain 1.50 %,<br> Temperature 320 °F
 ISO 11403-1 -2
41.3 MPa
<br>@Strain 3.00 %,<br> Temperature 160 °C
 5990 psi
<br>@Strain 3.00 %,<br> Temperature 320 °F
 ISO 11403-1 -2
91.7 MPa
<br>@Strain 1.50 %,<br> Temperature 40.0 °C
 13300 psi
<br>@Strain 1.50 %,<br> Temperature 104 °F
 ISO 11403-1 -2
114 MPa
<br>@Strain 3.00 %,<br> Temperature 40.0 °C
 16500 psi
<br>@Strain 3.00 %,<br> Temperature 104 °F
 ISO 11403-1 -2
122 MPa
<br>@Strain 1.50 %,<br> Temperature 23.0 °C
 17700 psi
<br>@Strain 1.50 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
138 MPa
<br>@Strain 1.50 %,<br> Temperature 0.000 °C
 20000 psi
<br>@Strain 1.50 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
149 MPa
<br>@Strain 1.50 %,<br> Temperature -20.0 °C
 21600 psi
<br>@Strain 1.50 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
159 MPa
<br>@Strain 1.50 %,<br> Temperature -40.0 °C
 23100 psi
<br>@Strain 1.50 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
10.0 MPa
<br>@Strain 0.175 %,<br> Time 3.60e+7 sec
 1450 psi
<br>@Strain 0.175 %,<br> Time 10000 hour
 isochronous; ISO 11403-1 -2
10.0 MPa
<br>@Strain 0.126 %,<br> Time 36000 sec
 1450 psi
<br>@Strain 0.126 %,<br> Time 10.0 hour
 isochronous; ISO 11403-1 -2
10.0 MPa
<br>@Strain 0.115 %,<br> Time 3600 sec
 1450 psi
<br>@Strain 0.115 %,<br> Time 1.00 hour
 isochronous; ISO 11403-1 -2
10.0 MPa
<br>@Strain 0.142 %,<br> Time 360000 sec
 1450 psi
<br>@Strain 0.142 %,<br> Time 100 hour
 isochronous; ISO 11403-1 -2
10.0 MPa
<br>@Strain 0.159 %,<br> Time 3.60e+6 sec
 1450 psi
<br>@Strain 0.159 %,<br> Time 1000 hour
 isochronous; ISO 11403-1 -2
40.0 MPa
<br>@Strain 0.603 %,<br> Time 360000 sec
 5800 psi
<br>@Strain 0.603 %,<br> Time 100 hour
 isochronous; ISO 11403-1 -2
50.0 MPa
<br>@Strain 0.889 %,<br> Time 3.60e+6 sec
 7250 psi
<br>@Strain 0.889 %,<br> Time 1000 hour
 isochronous; ISO 11403-1 -2
50.0 MPa
<br>@Strain 0.682 %,<br> Time 36000 sec
 7250 psi
<br>@Strain 0.682 %,<br> Time 10.0 hour
 isochronous; ISO 11403-1 -2
50.0 MPa
<br>@Strain 1.02 %,<br> Time 3.60e+7 sec
 7250 psi
<br>@Strain 1.02 %,<br> Time 10000 hour
 isochronous; ISO 11403-1 -2
60.0 MPa
<br>@Strain 0.768 %,<br> Time 3600 sec
 8700 psi
<br>@Strain 0.768 %,<br> Time 1.00 hour
 isochronous; ISO 11403-1 -2
80.0 MPa
<br>@Strain 1.53 %,<br> Time 360000 sec
 11600 psi
<br>@Strain 1.53 %,<br> Time 100 hour
 isochronous; ISO 11403-1 -2
Elongation at Break 2.7 %
2.7 %
ISO 527-1/-2
Tensile Modulus 10.0 GPa
1450 ksi
ISO 527-1/-2
3.59 GPa
<br>@Temperature 150 °C
 520 ksi
<br>@Temperature 302 °F
 ISO 11403-1 -2
4.20 GPa
<br>@Temperature 90.0 °C
 610 ksi
<br>@Temperature 194 °F
 Dynamic; ISO 11403-1 -2
4.78 GPa
<br>@Temperature 90.0 °C
 693 ksi
<br>@Temperature 194 °F
 ISO 11403-1 -2
7.65 GPa
<br>@Temperature 40.0 °C
 1110 ksi
<br>@Temperature 104 °F
 ISO 11403-1 -2
10.5 GPa
<br>@Temperature -40.0 °C
 1520 ksi
<br>@Temperature -40.0 °F
 Dynamic; ISO 11403-1 -2
10.66 GPa
<br>@Temperature -40.0 °C
 1546 ksi
<br>@Temperature -40.0 °F
 ISO 11403-1 -2
Flexural Strength 200 MPa
29000 psi
ISO 178
Flexural Modulus 9.00 GPa
1310 ksi
ISO 178
Shear Modulus 0.550 GPa
<br>@Temperature 160 °C
 79.8 ksi
<br>@Temperature 320 °F
 Dynamic; ISO 11403-1 -2
0.696 GPa
<br>@Temperature 120 °C
 101 ksi
<br>@Temperature 248 °F
 Dynamic; ISO 11403-1 -2
1.00 GPa
<br>@Temperature 70.0 °C
 145 ksi
<br>@Temperature 158 °F
 Dynamic; ISO 11403-1 -2
1.94 GPa
<br>@Temperature 20.0 °C
 281 ksi
<br>@Temperature 68.0 °F
 Dynamic; ISO 11403-1 -2
2.09 GPa
<br>@Temperature -20.0 °C
 303 ksi
<br>@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
2.21 GPa
<br>@Temperature -50.0 °C
 321 ksi
<br>@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Secant Modulus 1.82 GPa
<br>@Strain 3.50 %,<br> Temperature 100 °C
 264 ksi
<br>@Strain 3.50 %,<br> Temperature 212 °F
 ISO 11403-1 -2
1.99 GPa
<br>@Strain 3.50 %,<br> Temperature 80.0 °C
 289 ksi
<br>@Strain 3.50 %,<br> Temperature 176 °F
 ISO 11403-1 -2
2.95 GPa
<br>@Strain 1.50 %,<br> Temperature 100 °C
 428 ksi
<br>@Strain 1.50 %,<br> Temperature 212 °F
 ISO 11403-1 -2
3.29 GPa
<br>@Strain 3.50 %,<br> Temperature 40.0 °C
 477 ksi
<br>@Strain 3.50 %,<br> Temperature 104 °F
 ISO 11403-1 -2
3.30 GPa
<br>@Strain 1.50 %,<br> Temperature 80.0 °C
 479 ksi
<br>@Strain 1.50 %,<br> Temperature 176 °F
 ISO 11403-1 -2
4.44 GPa
<br>@Strain 0.250 %,<br> Temperature 100 °C
 644 ksi
<br>@Strain 0.250 %,<br> Temperature 212 °F
 ISO 11403-1 -2
4.84 GPa
<br>@Strain 0.250 %,<br> Temperature 80.0 °C
 702 ksi
<br>@Strain 0.250 %,<br> Temperature 176 °F
 ISO 11403-1 -2
6.11 GPa
<br>@Strain 1.50 %,<br> Temperature 40.0 °C
 887 ksi
<br>@Strain 1.50 %,<br> Temperature 104 °F
 ISO 11403-1 -2