SABIC Innovative Plastics LNP LUBRICOMP NXCY620 PC+ABS

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP NXCY620 PC+ABS.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* LUBRICOMP* NXCY620 is a compound based on Cycoloy* XCY620 containing Silicone. Added feature of this material is: Lubricant.

Physical Properties	Metric	English	Comments
Specific Gravity	1.14 g/cc	1.14 g/cc	ASTM D792
Density	1.13 g/cc	0.0408 lb/inÂ³	ASTM D792
Moisture Absorption	0.150 %	0.150 %	50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.0060 - 0.0080 cm/cm @Time 86400 sec	0.0060 - 0.0080 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.0060 - 0.0080 cm/cm @Time 86400 sec	0.0060 - 0.0080 in/in @Time 24.0 hour	ASTM D955
Melt Flow	30 g/10 min @Load 5.00 kg, Temperature 260 Â°C	30 g/10 min @Load 11.0 lb, Temperature 500 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	40.0 MPa	5800 psi	Type I, 5 mm/min; ASTM D638
	42.0 MPa	6090 psi	5 mm/min; ISO 527
Tensile Strength, Yield	49.0 MPa	7110 psi	5 mm/min; ISO 527
	51.0 MPa	7400 psi	Type I, 5 mm/min; ASTM D638
Elongation at Break	31 %	31 %	Type I, 50 mm/min; ASTM D638
	50 %	50 %	50 mm/min; ISO 527
Elongation at Yield	4.7 %	4.7 %	Type I, 50 mm/min; ASTM D638
	4.9 %	4.9 %	50 mm/min; ISO 527
Tensile Modulus	2.09 GPa	303 ksi	1 mm/min; ISO 527
	2.19 GPa	318 ksi	5 mm/min; ASTM D638
Flexural Strength	77.0 MPa	11200 psi	ISO 178
	79.0 MPa	11500 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	2.11 GPa	306 ksi	2 mm/min; ISO 178
	2.22 GPa	322 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	6.54 J/cm	12.3 ft-lb/in	ASTM D256
Izod Impact, Unnotched	NB	NB	ASTM D4812
Izod Impact, Notched (ISO)	48.0 kJ/mÂ²	22.8 ft-lb/inÂ²	80104; ISO 180/1A
	28.0 kJ/mÂ² @Temperature -40.0 Â°C	13.3 ft-lb/inÂ² @Temperature -40.0 Â°F	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	NB	NB	80104; ISO 180/1U
Charpy Impact, Notched	5.10 J/cmÂ²	24.3 ft-lb/inÂ²	ISO 179/2C
	3.90 J/cmÂ² @Temperature -30.0 Â°C	18.6 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179/2C
Coefficient of Friction, Dynamic	0.23	0.23	ASTM D3702 Modified
Coefficient of Friction, Static	0.18	0.18	ASTM D3702 Modified
K (wear) Factor	14.1 x 10^-8 mmÂ³/N-M	7.00 x 10^-10 inÂ³-min/ft-lb-hr	Ring; ASTM D3702 Modified
	2520 x 10^-8 mmÂ³/N-M	1250 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	73.0 Âµm/m-Â°C @Temperature -30.0 - 30.0 Â°C	40.6 Âµin/in-Â°F @Temperature -22.0 - 86.0 Â°F	ASTM D696
CTE, linear, Transverse to Flow	78.0 Âµm/m-Â°C @Temperature -30.0 - 30.0 Â°C	43.3 Âµin/in-Â°F @Temperature -22.0 - 86.0 Â°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	125 Â°C	257 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi)	110 Â°C	230 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	108 Â°C @Thickness 3.20 mm	226 Â°F @Thickness 0.126 in	unannealed; ASTM D648