SABIC Innovative Plastics Xenoy® X6125 PBT+PC

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xenoy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Xenoy® X6125 PBT+PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unreinforced, impact modified, thermoplastic alloy (PBT+PC). High impact strength while retaining mechanical and thermal properties.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.24 g/cc
1.24 g/cc
ASTM D 792
Density 1.24 g/cc
0.0448 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.080 %
0.080 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.13 %

@Temperature 23.0 °C
 0.13 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0165 - 0.018 cm/cm

@Thickness 3.20 mm
 0.0165 - 0.018 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 17 g/10 min

@Load 1.20 kg,
Temperature 266 °C
 17 g/10 min

@Load 2.65 lb,
Temperature 511 °F
 ASTM D 1238
28 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 28 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 39.0 MPa
5660 psi
Type I, 50 mm/min; ASTM D 638
39.0 MPa
5660 psi
50 mm/min; ISO 527
Tensile Strength, Yield 47.0 MPa
6820 psi
50 mm/min; ISO 527
51.0 MPa
7400 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 130 %
130 %
50 mm/min; ISO 527
137 %
137 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 4.0 %
4.0 %
Type I, 50 mm/min; ASTM D 638
4.0 %
4.0 %
50 mm/min; ISO 527
Tensile Modulus 2.23 GPa
323 ksi
50 mm/min; ASTM D 638
2.28 GPa
331 ksi
1 mm/min; ISO 527
Flexural Yield Strength 70.0 MPa
10200 psi
2 mm/min; ISO 178
82.0 MPa
11900 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 1.86 GPa
270 ksi
2 mm/min; ISO 178
2.29 GPa
332 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 1.22 J/cm

@Temperature -30.0 °C
 2.29 ft-lb/in

@Temperature -22.0 °F
 ASTM D 256
8.85 J/cm

@Temperature 23.0 °C
 16.6 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Notched (ISO) 9.00 kJ/m²

@Temperature -30.0 °C
 4.28 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
64.0 kJ/m²

@Temperature 23.0 °C
 30.5 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 7.50 J/cm²

@Temperature 23.0 °C
 35.7 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 59.0 J

@Temperature 23.0 °C
 43.5 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 88.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 48.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
88.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 48.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 50.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
90.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 50.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 115 °C

@Thickness 3.20 mm
 239 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 57.0 °C
135 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
64.0 °C

@Thickness 3.20 mm
 147 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Vicat Softening Point 130 °C
266 °F
Rate B/50; ASTM D 1525
132 °C
270 °F
Rate B/50; ISO 306
135 °C
275 °F
Rate B/120; ISO 306