SABIC Innovative Plastics LNP LUBRICOMP JFL34 PES

Category	Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP JFL34 PES.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* LUBRICOMP* JFL34 is a compound based on Polyethersulfone resin containing 20% Glass Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant.

Physical Properties	Metric	English	Comments
Specific Gravity	1.61 g/cc	1.61 g/cc	ASTM D792
Density	1.61 g/cc	0.0582 lb/inÂ³	ISO 1183
Moisture Absorption	0.350 %	0.350 %	50% RH, 24 hrs; ASTM D570
	0.520 %	0.520 %	23Â°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.0030 - 0.0050 cm/cm @Time 86400 sec	0.0030 - 0.0050 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.0050 - 0.0070 cm/cm @Time 86400 sec	0.0050 - 0.0070 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	94.0 MPa	13600 psi	5 mm/min; ISO 527
	97.0 MPa	14100 psi	Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield	103 MPa	14900 psi	5 mm/min; ISO 527
	104 MPa	15100 psi	Type I, 5 mm/min; ASTM D638
Elongation at Break	2.5 %	2.5 %	5 mm/min; ISO 527
	2.5 %	2.5 %	Type I, 5 mm/min; ASTM D638
Elongation at Yield	2.5 %	2.5 %	5 mm/min; ISO 527
	2.5 %	2.5 %	Type I, 5 mm/min; ASTM D638
Tensile Modulus	7.03 GPa	1020 ksi	1 mm/min; ISO 527
	7.07 GPa	1030 ksi	50 mm/min; ASTM D638
Flexural Strength	146 MPa	21200 psi	1.3 mm/min, 50 mm span; ASTM D790
	147 MPa	21300 psi	ISO 178
Flexural Yield Strength	147 MPa	21300 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	6.02 GPa	873 ksi	1.3 mm/min, 50 mm span; ASTM D790
	6.30 GPa	914 ksi	2 mm/min; ISO 178
Izod Impact, Notched	0.730 J/cm	1.37 ft-lb/in	ASTM D256
Izod Impact, Unnotched	5.38 J/cm	10.1 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	7.00 kJ/mÂ²	3.33 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	32.0 kJ/mÂ²	15.2 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	14.0 J @Temperature 23.0 Â°C	10.3 ft-lb @Temperature 73.4 Â°F	ASTM D3763
Impact Test	3.00 J	2.21 ft-lb	Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic	0.46	0.46	ASTM D3702 Modified
Coefficient of Friction, Static	0.63	0.63	ASTM D3702 Modified
K (wear) Factor	14.1 x 10^-8 mmÂ³/N-M	7.00 x 10^-10 inÂ³-min/ft-lb-hr	Ring; ASTM D3702 Modified
	117 x 10^-8 mmÂ³/N-M	58.0 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	32.0 Âµm/m-Â°C @Temperature -30.0 - 30.0 Â°C	17.8 Âµin/in-Â°F @Temperature -22.0 - 86.0 Â°F	ASTM D696
CTE, linear, Transverse to Flow	41.0 Âµm/m-Â°C @Temperature -30.0 - 30.0 Â°C	22.8 Âµin/in-Â°F @Temperature -22.0 - 86.0 Â°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	220 Â°C	428 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
	219 Â°C @Thickness 3.20 mm	426 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	212 Â°C	414 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	212 Â°C @Thickness 3.20 mm	414 Â°F @Thickness 0.126 in	unannealed; ASTM D648