Honeywell Capran® Emblem™ 1200 Bi-Axially Oriented Nylon Film
| Category | Polymer , Film , Thermoplastic , Nylon |
| Manufacturer | Honeywell |
| Trade Name | Capran® Emblem™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell Capran® Emblem™ 1200 Bi-Axially Oriented Nylon Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Capran® Emblem™ 1200 is a bi-axially oriented nylon film. It is a versatile and robust film that satisfies many packaging needs, and has superior resistance to oils, fats, hydrocarbons, and many solvents. It is also microwavable, making it an excellent choice for lidding stock.Applications: bag-on-box packaging, packaging for processed meats, cheese, meat snacks, coffee bricks, coffee bags, and pet food, agricultural bags, stand-up shampoo pouches, book covers and metallized balloons.Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0420 lb/in³ | Yield Density |
| Water Vapor Transmission | 357 - 404 g/m²/day | 23.0 - 26.0 g/100 in²/day | 100°F / 100%RH); ASTM F1249 |
| Oxygen Transmission Rate | 54.32 - 69.84 cc/m²/day | 3.498 - 4.498 cc/100 in²/day | 77°F / 0% / RH; ASTM D3985 |
| Thickness | 12.2 microns | 0.480 mil |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 60 - 90 % | 60 - 90 % | ASTM D882 |
| Film Elongation at Break, TD | 60 - 90 % | 60 - 90 % | ASTM D882 |
| Secant Modulus, MD | 2.41 - 3.92 GPa | 350 - 569 ksi | ASTM D882 |
| Secant Modulus, TD | 2.48 - 3.59 GPa | 360 - 521 ksi | ASTM D882 |
| Coefficient of Friction | 0.17 - 0.28 | 0.17 - 0.28 | film to stainless steel; ASTM D1894 |
| 0.55 - 0.74 | 0.55 - 0.74 | film to film; ASTM D1894 | |
| Tear Strength Test | 1100 - 1500 | 1100 - 1500 | graves tear, grams/mil (initial); ASTM D1004 |
| Elmendorf Tear Strength, MD | 0.4102 - 0.6563 g/micron | 10.42 - 16.67 g/mil | |
| Film Tensile Strength at Break, MD | 234 - 303 MPa | 34000 - 44000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 193 - 303 MPa | 28000 - 44000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 1.6 - 2.5 % | 1.6 - 2.5 % | 320°F / 160°C - 5 minutes; ASTM D1204 |
| Shrinkage, TD | 0.20 - 0.70 % | 0.20 - 0.70 % | 320°F / 160°C - 5 minutes; ASTM D1204 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 3.0 % | <= 3.0 % | ASTM D1003 |
| Gloss | 160 - 180 % | 160 - 180 % | at 20° |
Users viewing this material also viewed the following:
- Polymer Resources PC/TP-GP3-IM PC/Polyester Alloy, Impact Modified
- Rogers Corporation Bisco® MF1 6535 - 35 Silicone, High Performance Foam, Indentation Force Material
- Premix Thermoplastics PRE-ELEC® CP 1315 (discontinued **)
- Nitriflex N-8 NBR - Nitrile Rubber
- DuPont Bynel® 41E689 Adhesive Resin (discontinued **)
- Overview of materials for Liquid Crystal Polymer (LCP), Mineral Filled
- Sylvin Technologies 8999-60 Natural PVC Extrusion Compound
- A. Schulman Aqualoy® 645 Glass Fiber Reinforced Hydrolysis Resistant Nylon 66
- Hexcel® HexForce™ 130 Carbon Fabric
- SABIC Innovative Plastics LNP Thermocomp JF002E PES
Copyright © lookpolymers.com All Rights Reserved