SABIC Innovative Plastics LNP LUBRICOMP CBL36XXC PS

Category Polymer , Thermoplastic , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP CBL36XXC PS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* CBL36XXC is a compound based on Polystyrene resin containing 30% Glass Bead and 15% PTFE. Added features of this material include: Wear Resistant.
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0050 cm/cm

@Time 86400 sec
 0.0050 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 22.0 MPa
3190 psi
ASTM D638
Elongation at Break 2.0 %
2.0 %
ASTM D638
Tensile Modulus 5.56 GPa
806 ksi
50 mm/min; ASTM D638
Flexural Strength 41.0 MPa
5950 psi
ASTM D790
Flexural Modulus 4.08 GPa
592 ksi
ASTM D790
Izod Impact, Notched 0.100 J/cm
0.187 ft-lb/in
ASTM D256
Izod Impact, Unnotched 0.760 J/cm
1.42 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 77.0 °C

@Thickness 3.20 mm
 171 °F

@Thickness 0.126 in
 unannealed; ASTM D648