Honeywell Capran® Emblem™ MT2500 Bi-Axially Oriented Nylon 6 Film
| Category | Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Film Grade |
| Manufacturer | Honeywell |
| Trade Name | Capran® Emblem™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell Capran® Emblem™ MT2500 Bi-Axially Oriented Nylon 6 Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Capran® Emblem™ MT2500 is a 1.00 mil (25 micron) biaxially oriented nylon 6 film with a metallized barrier coating.Applications: Capron® Emblem™ MT2500 is well suited for high barrier packaging solutions. Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0420 lb/in³ | Yield Density |
| Water Vapor Transmission | 2.60 g/m²/day | 0.167 g/100 in²/day | 100°F / 100%RH); ASTM F1249 |
| Oxygen Transmission Rate | 1.10 cc/m²/day | 0.0708 cc/100 in²/day | 77°F / 0% / RH; ASTM D3985 |
| Thickness | 25.4 microns | 1.00 mil | |
| Surface Tension | >= 50 dynes/cm | >= 50 dynes/cm | untreated side; ASTM D5946 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 70 - 110 % | 70 - 110 % | ASTM D882 |
| Film Elongation at Break, TD | 60 - 90 % | 60 - 90 % | ASTM D882 |
| Secant Modulus, MD | 2.413 - 3.551 GPa | 350.0 - 515.0 ksi | ASTM D882 |
| Secant Modulus, TD | 2.275 - 3.282 GPa | 330.0 - 476.0 ksi | ASTM D882 |
| Coefficient of Friction | 0.21 - 0.41 | 0.21 - 0.41 | film to stainless steel; ASTM D1894 |
| 0.65 - 0.86 | 0.65 - 0.86 | film to film; ASTM D1894 | |
| Tear Strength Test | 1150 - 1475 | 1150 - 1475 | graves tear TD, grams/mil; ASTM D1004 |
| 1150 - 1500 | 1150 - 1500 | graves tear MD, grams/mil; ASTM D1004 | |
| Film Tensile Strength at Break, MD | 234 - 283 MPa | 34000 - 41000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 221 - 283 MPa | 32000 - 41000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 1.6 - 2.3 % | 1.6 - 2.3 % | 320°F / 160°C - 5 minutes; ASTM D1204 |
| Shrinkage, TD | 0.20 - 0.70 % | 0.20 - 0.70 % | 320°F / 160°C - 5 minutes; ASTM D1204 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Helium Transition Rate | max 93 cc/m2/day | ASTM 1434 |
Users viewing this material also viewed the following:
- MV Labs K1090 K2S2O8 Potassium persulfate
- RheTech Products FT4900-745UV Thermoplastic Polyolefin, UV Stabilized, CJM Medium Khaki Solid
- SABIC Innovative Plastics LNP LUBRICOMP RFL36L PA 66
- Teknor Apex APEX® 87-L101F-3 Polyvinyl Chloride, Flexible
- SMAC CABLE® 2521S-50-08 Damping Material
- Corning Gorilla® Glass 4 Touch Screen Glass
- Covestro Desmopan® DP 1490A Polyurethane
- EMS-Grivory Grivory® TR 55 LZ PA12/MACMI
- Bhansali Engineering Abstron BL60 Impact modifier for PVC
Copyright © lookpolymers.com All Rights Reserved