- Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
- SABIC Innovative Plastics Geloy FXTW30PE ASA
SABIC Innovative Plastics Geloy FXTW30PE ASA
| Category | Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | GELOY |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Geloy FXTW30PE ASA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Pearlescent GELOY ASA resin with copper-look for capstock extrusion. Outstanding weatherability.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D 792 |
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00 - 0.0010 cm/cm @Thickness 3.20 mm |
0.00 - 0.0010 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 0.60 g/10 min @Load 3.80 kg, Temperature 200 °C |
0.60 g/10 min @Load 8.38 lb, Temperature 392 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 39.0 MPa | 5660 psi | Type I, 5 mm/min; ASTM D 638 |
| 48.0 MPa | 6960 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | Type I, 5 mm/min; ASTM D 638 |
| 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 14 % | 14 % | Type I, 5 mm/min; ASTM D 638 |
| 29 % | 29 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 3.3 % | 3.3 % | Type I, 5 mm/min; ASTM D 638 |
| 3.6 % | 3.6 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.67 GPa | 387 ksi | 5 mm/min; ASTM D 638 |
| 2.75 GPa | 399 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 76.0 MPa | 11000 psi | 2 mm/min; ISO 178 |
| 77.0 MPa | 11200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 2.75 GPa | 399 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 2.78 GPa | 403 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.340 J/cm @Temperature -30.0 °C |
0.637 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 0.670 J/cm @Temperature 23.0 °C |
1.26 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Impact Test | 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 95.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
53.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 108 µm/m-°C @Temperature -40.0 - 40.0 °C |
60.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 76.0 °C @Thickness 3.20 mm |
169 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 86.0 °C | 187 °F | Rate B/50; ISO 306 |
| 89.0 °C | 192 °F | Rate B/50; ASTM D 1525 |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene® N 3980/G Acrylonitrile-Butadiene Rubber
- DuPont Performance Polymers Crastin® S600F40 NC010 PBT (Unverified Data**)
- Kleerdex Kydex® P55 Acrylic/PVC Extrusion Compound (discontinued **)
- Lord Adhesives Metech 6103 Silver Conductor
- Mitsubishi Iupilon® H3000UR 30 MFI, UV Stabilized Polycarbonate With Release
- ExxonMobil Gargoyle Arctic 230 SHC 200 Series
- A. Schulman POLYBATCH™ Gardenia P80515PF Concentrate Based In Polypropylene
- ExxonMobil Bicor™ 25 ARW OPP Film
- Asahi Kasei Thermofil N7-9900-1600 Unreinforced, High Impact, Heat Stabilized
Copyright © lookpolymers.com All Rights Reserved