SABIC Innovative Plastics Cycoloy® MC9000 PC+ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycoloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycoloy® MC9000 PC+ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AUTOMOTIVE. PC+ABS; high heat resistant. Ductile at room temperature. Excellent flow.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 22 g/10 min @Load 5.00 kg, Temperature 260 °C |
22 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 59.0 MPa | 8560 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 75 % | 75 % | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D 638 |
| Tensile Modulus | 2.20 GPa | 319 ksi | 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 86.0 MPa | 12500 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.37 GPa | 344 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 2.67 J/cm @Temperature -30.0 °C |
5.00 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 6.40 J/cm @Temperature 23.0 °C |
12.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Impact Test | 58.0 J @Temperature -30.0 °C |
42.8 ft-lb @Temperature -22.0 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| 61.0 J @Temperature 23.0 °C |
45.0 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 72.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 126 °C @Thickness 3.20 mm |
259 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C @Thickness 3.20 mm |
230 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Nilit Nilamid B3 H ZB Unfilled, Low Temperature Impact Resistant PA6
- SABIC Innovative Plastics NORYL PX2801Z PPE+HIPS (Asia Pacific)
- Borealis PS65C40 Polypropylene Compound, Mineral Filled
- Williams Advanced Alloys Wambraze™ WB853 Solder
- DSM Stanyl® TW341 (DAM) Nylon 46 Heat Stabilized, Lubricated (North America)
- EMS-Grivory Grivory® HB 5299 HV PA*
- Dow LDPE 530A Low Density Polyethylene, Blown Film Grade
- ConocoPhillips Hydroclear® 150 Rolling Oil
- A. Schulman POLYBATCH™ Green 30424 Concentrate Based In Polyethylene
- Quadrant EPP Quadrant PSU unfilled, extruded (ISO Data)
Copyright © lookpolymers.com All Rights Reserved