- SABIC Innovative Plastics Cycoloy® MC8100 PC+ABS (Asia Pacific)
SABIC Innovative Plastics Cycoloy® MC8100 PC+ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycoloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycoloy® MC8100 PC+ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Extrusion blowmolding grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption at Equilibrium | 0.40 % | 0.40 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 100 % | 100 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.06 GPa | 299 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 77.0 MPa | 11200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.06 GPa | 299 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D256 |
| 4.27 J/cm @Temperature -30.0 °C |
8.00 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 47.0 J @Temperature -30.0 °C |
34.7 ft-lb @Temperature -22.0 °F |
ASTM D3763 |
| 54.0 J @Temperature 23.0 °C |
39.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 81.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C @Thickness 3.20 mm |
219 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Lubrizol Advanced Materials Pearlstick® 45-40/11S Polycaprolactone based TPU (discontinued **)
- Parker Chomerics SOFT-SHIELD® 4006 Low Closure Force, Foam Core EMI Gasket
- Karina E 898-10/161-IS-RG White PVC Compound
- Kennametal Stellite Tribaloy® T-800
- Solvay TECHNYL® C 236SI PA6, DRY
- Techmer ES HiFill® PA6/6 GF60 TL10 60% Glass Filled
- SCG Chemicals EL-Leneâ„¢ L2009FA Linear Low Density Polyethylene Film
- Braskem CP 741 Extrusion Polypropylene Heterophasic Copolymer
- Reade Advanced Materials Titanium Hydride Powder (TiH2)
Copyright © lookpolymers.com All Rights Reserved