SABIC Innovative Plastics Cycoloy® C4220K PC+ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycoloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycoloy® C4220K PC+ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Cycoloy* C4220K resin is an injection moldable 20% glass reinforced non FR PC-ABS.
Key features include improved Knit Line strength, good flow, excellent strength & rigidity, heat resistance & hydrolytic stability.
Ideal for small to medium size & thin wall applications that required rigid frame for reinforcement with good Knit Line strength.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.12 % | 0.12 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.60 % @Temperature 23.0 °C |
0.60 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 11 g/10 min @Load 5.00 kg, Temperature 260 °C |
11 g/10 min @Load 11.0 lb, Temperature 500 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 12 g/10 min @Load 5.00 kg, Temperature 260 °C |
12 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 96 | 96 | ISO 2039-2 |
| Hardness, Rockwell R | 119 | 119 | ISO 2039-2 |
| Tensile Strength at Break | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 6.00 GPa | 870 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 125 MPa | 18100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.40 GPa | 783 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 1.00 J/cm @Temperature 23.0 °C |
1.87 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 5.50 J/cm @Temperature 23.0 °C |
10.3 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
80*10*3; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
80*10*3; ISO 180/1U |
| Charpy Impact Unnotched | 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 26.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
14.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 81.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 135 °C | 275 °F | Rate B/50; ISO 306 |
| 137 °C | 279 °F | Rate B/120; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.50e+16 ohm-cm | 3.50e+16 ohm-cm | ASTM D 257 |
| Surface Resistance | 3.50e+16 ohm | 3.50e+16 ohm | ASTM D 257 |
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.4 @Frequency 1000 Hz |
3.4 @Frequency 1000 Hz |
IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm @Thickness 1.60 mm |
762 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 |
| 40.0 kV/mm @Thickness 0.800 mm |
1020 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |
| Dissipation Factor | 0.0080 @Frequency 1000 Hz |
0.0080 @Frequency 1000 Hz |
IEC 60250 |
| 0.011 @Frequency 1.00e+6 Hz |
0.011 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | pass | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- PolyOne Stat-Tech™ AS-08CF/000 Black Acrylonitrile Butadiene Styrene (ABS), Carbon Fiber Reinforced (disconti
- Rostone Rosite® 3950ES SMC Thermoset Polyester, 25% Glass Reinforced (discontinued **)
- Fainplast Compounds RH 212/W Rigid PVC, Antishock Extrusion
- Huntsman Tactix 742 Multifunctional Resin
- Garlock 505 CPE Sheet Rubber
- Techmer ES Statiblend® HIPS E AS
- DSM Novamid® 1015GH35 BK37 PA6-GF35
- Eurostar Staramide ACF2 PA66, 10% Carbon Fiber Reinforced, Heat stabilized, Injection Molding
- Aptek DI-STRATE 95217 Microwave/RF Foam Substrate
- DSM Akulon® K224-PG3 Impact Modified Nylon 6-15% Glass Reinforced (European Grade) (Cond)
Copyright © lookpolymers.com All Rights Reserved