SABIC Innovative Plastics Cycoloy® C2800 PC+ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® C2800 PC+ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Non-chlorinated and non-brominated flame retardant PC+ABS offering balanced flow and impact properties for various applications.
Physical Properties Metric English Comments
Specific Gravity 1.17 g/cc
1.17 g/cc
ASTM D792
1.18 g/cc
1.18 g/cc
color; ASTM D792
Water Absorption 0.10 %

@Time 86400 sec
 0.10 %

@Time 24.0 hour
 ASTM D570
Moisture Absorption at Equilibrium 0.40 %
0.40 %
ASTM D570
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 16 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 16 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength, Yield 58.0 MPa
8410 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 50 %
50 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 5.0 %
5.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.68 GPa
389 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 96.0 MPa
13900 psi
2.6 mm/min, 100 mm span; ASTM D790
Flexural Modulus 2.68 GPa
389 ksi
2.6 mm/min, 100 mm span; ASTM D790
Izod Impact, Notched 4.27 J/cm
8.00 ft-lb/in
ASTM D256
Dart Drop, Total Energy 58.0 J

@Temperature 23.0 °C
 42.8 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 72.0 µm/m-°C

@Temperature -40.0 - 60.0 °C
 40.0 µin/in-°F

@Temperature -40.0 - 140 °F
 ASTM E 831
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature -40.0 - 60.0 °C
 40.0 µin/in-°F

@Temperature -40.0 - 140 °F
 ASTM E 831
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 1.8 MPa (264 psi) 73.0 °C

@Thickness 3.20 mm
 163 °F

@Thickness 0.126 in
 unannealed; ASTM D648
80.0 °C

@Thickness 6.40 mm
 176 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 90.0 °C
194 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical with Impact 70.0 °C
158 °F
UL 746B
UL RTI, Mechanical without Impact 80.0 °C
176 °F
UL 746B
Flammability, UL94 V-2

@Thickness 0.880 mm
 V-2

@Thickness 0.0346 in
 UL 94
V-0

@Thickness 1.47 mm
 V-0

@Thickness 0.0579 in
 UL 94
5VB

@Thickness 2.31 mm
 5VB

@Thickness 0.0909 in
 UL 94
Oxygen Index 35 %
35 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
ASTM D257
Surface Resistance >= 1.00e+14 ohm
>= 1.00e+14 ohm
ASTM D257
Dielectric Constant 3.0

@Frequency 50.0 - 60.0 Hz
 3.0

@Frequency 50.0 - 60.0 Hz
 ASTM D150
3.0

@Frequency 100 Hz
 3.0

@Frequency 100 Hz
 ASTM D150
Dielectric Strength 17.9 kV/mm

@Thickness 3.20 mm
 455 kV/in

@Thickness 0.126 in
 in oil; ASTM D149
Dissipation Factor 0.0048

@Frequency 50.0 - 60.0 Hz
 0.0048

@Frequency 50.0 - 60.0 Hz
 ASTM D150
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten; ASTM D495
Comparative Tracking Index 400 - 600 V
400 - 600 V
UL 746A
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
UL 746A