SABIC Innovative Plastics Cycolac® GRM2600L ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® GRM2600L ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High Impact , good chemical resistance sheet grade ABS designed for refrigerator liner applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0045 - 0.0065 cm/cm @Thickness 3.20 mm |
0.0045 - 0.0065 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 2.5 g/10 min @Load 10.0 kg, Temperature 220 °C |
2.5 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 35.0 MPa | 5080 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 55 % | 55 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 75.0 MPa | 10900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 4.00 J/cm | 7.49 ft-lb/in | ASTM D256 |
| Dart Drop, Total Energy | 46.0 J @Temperature 23.0 °C |
33.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C @Thickness 3.20 mm |
212 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 3.20 mm |
185 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 113 °C | 235 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- PolyOne Gravi-Tech™ GRV-NY-050-CU-NAT Polyamide 6 (Nylon 6)
- Pacific Sintered Materials FN-250-S Nickel Iron Powdered Metal
- Honeywell Capran® Oxyshield™ OBS Monoaxially Oriented, Co-Extruded Nylon 6/EVOH/Nylon 6 Clear Film
- Lehmann & Voss LUVOCOM® 1115/XCF/40 PEK, with carbon fiber
- Kennametal Stellite Deloro® N-6 PM with P/M Processing
- Hexcel® HexForce™ 2523 Fiber Glass Fabric
- Americas Styrenics EB6400 High Impact Polystyrene
- Chem Polymer Chemlon 130 GVH Nylon 66, 30% Glass Fiber Reinforced
- Fibre Glast RAE 2426 / 2177 Epoxy (discontinued **)
Copyright © lookpolymers.com All Rights Reserved