SABIC Innovative Plastics Cycolac® FXS600AR ABS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® FXS600AR ABS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Visual Ares effect Cycolac ABS material with excellent flow properties.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.0 % | 1.0 % | ISO 62 |
| Melt Index of Compound | 10 g/10 min @Load 5.00 kg, Temperature 220 °C |
10 g/10 min @Load 11.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 33 g/10 min @Load 10.0 kg, Temperature 220 °C |
33 g/10 min @Load 22.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 35.0 MPa | 5080 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 28 % | 28 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 2.0 % | 2.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.35 GPa | 341 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 66.0 MPa | 9570 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.25 GPa | 326 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| 10.0 kJ/m² @Temperature 0.000 °C |
4.76 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
50.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
50.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 95.0 °C | 203 °F | Rate B/50; ISO 306 |
| 98.0 °C | 208 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Nylene® Norpex® AX225 HI PPE (Polyphenylene Ether), High Impact Grade
- Rochling Engineered Plastics Polystone® G HDPE Extruded Sheet
- Total Lacqrene® 1250 Crystal Polystyrene (discontinued **)
- LATI LAXTAR G/30 30% Glass Reinforced LCP (discontinued **)
- Fine Organics FINALUX G 321 Lubricant Additive
- Mid-Mountain Materials CERMEX® MT1000 Needled Fiberglass Mat
- Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2075°F (1135°C)
- Styron MAGNUMâ„¢ 357 HP Acrylonitrile Butadiene Styrene (ABS) Resin
- Colorite Polymers CS1539GP Wire and Cable Insulation Vinyl Compound
- 3M 7045W Screen Printable Vinyl Performance Label Products
Copyright © lookpolymers.com All Rights Reserved