Rogers Corporation RO3003 Ceramic-Filled PTFE Composite, High Frequency Circuit Material

Category Polymer , Thermoplastic , Fluoropolymer , PTFE , Polytetrafluoroethylene (PTFE), Glass Filled, Molded
Manufacturer Rogers Corporation
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Rogers Corporation RO3003 Ceramic-Filled PTFE Composite, High Frequency Circuit Material.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features and Benefits:
Physical Properties Metric English Comments
Density 2.10 g/cc
0.0759 lb/in³
Water Absorption <= 0.10 %
<= 0.10 %
D24/23; IPC-TM-2.4.8
Mechanical Properties Metric English Comments
Tensile Modulus 0.903 GPa
131 ksi
X, Y-Direction; ASTM D638
Peel Strength 2.23 kN/m
12.7 pli
Copper; 1/2 oz. EDC After Solder Float; IPC-TM-650 2.4.8
Thermal Properties Metric English Comments
CTE, linear 16.0 µm/m-°C

@Temperature -55.0 - 288 °C
 8.89 µin/in-°F

@Temperature -67.0 - 550 °F
 Y-Direction; ASTM D3386-94
17.0 µm/m-°C

@Temperature -55.0 - 288 °C
 9.44 µin/in-°F

@Temperature -67.0 - 550 °F
 X-Direction; ASTM D3386-94
25.0 µm/m-°C

@Temperature -55.0 - 288 °C
 13.9 µin/in-°F

@Temperature -67.0 - 550 °F
 Z-Direction; ASTM D3386-94
Specific Heat Capacity 0.900 J/g-°C
0.215 BTU/lb-°F
Calculated
Thermal Conductivity 0.500 W/m-K

@Temperature 80.0 °C
 3.47 BTU-in/hr-ft²-°F

@Temperature 176 °F
 Z Direction; ASTM C518
Decomposition Temperature 500 °C
932 °F
TGA; ASTM D3850
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
Cond. A; IPC 2.5.17.1
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
Cond. A; IPC 2.5.17.1
Dielectric Constant 2.96 - 3.04

@Frequency 1.00e+10 Hz
 2.96 - 3.04

@Frequency 1.00e+10 Hz
 Clamped stripline, Z-direction; IPC-TM-650 2.5.5.5
3.0

@Frequency 8.00e+9 - 4.00e+10 Hz
 3.0

@Frequency 8.00e+9 - 4.00e+10 Hz
 Differential Phase Length Method, Z-Direction
Dissipation Factor 0.0013

@Frequency 1.00e+10 Hz
 0.0013

@Frequency 1.00e+10 Hz
 IPC-TM-650 2.5.5.5
Descriptive Properties Value Comments
Dimensional Stability 0.01 mm/m
ASTM D257, Cond. A; X, Y-direction
Thermal Coefficient of Dielectric Constant 13 ppm/°C
IPC-TM-650 2.5.5.5; 10 GHz; 0°C to 100°C; Z-Direction