SABIC Innovative Plastics LNP LUBRICOMP UFL269SA PPA

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP UFL269SA PPA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* UFL269SA is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Heat Stabilized, Flame Retardant.
Physical Properties Metric English Comments
Density 1.71 g/cc
0.0618 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm

@Time 86400 sec
0.0020 - 0.0040 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0070 - 0.0090 cm/cm

@Time 86400 sec
0.0070 - 0.0090 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 162 MPa
23500 psi
ASTM D638
Elongation at Break 1.7 %
1.7 %
ASTM D638
Tensile Modulus 13.65 GPa
1980 ksi
50 mm/min; ASTM D638
Flexural Strength 227 MPa
32900 psi
ASTM D790
Flexural Modulus 12.82 GPa
1859 ksi
ASTM D790
Izod Impact, Notched 0.850 J/cm
1.59 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.61 J/cm
8.64 ft-lb/in
ASTM D4812
Coefficient of Friction, Dynamic 0.47
0.47
ASTM D3702 Modified
Coefficient of Friction, Static 0.38
0.38
ASTM D3702 Modified
K (wear) Factor 171 x 10-8 mm³/N-M
85.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 273 °C

@Thickness 3.20 mm
523 °F

@Thickness 0.126 in
unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94 by SABIC-IP