Resinoid 2002-4 Phenolic Molding, Fabric Reinforced

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Fabric Filled
Manufacturer Resinoid
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Resinoid 2002-4 Phenolic Molding, Fabric Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer.The Resinoid 2000 organic fiber reinforced series compounds feature mechanical strength, dimensional stability, and shock resistance
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ASTM D792A
Water Absorption 0.60 %
0.60 %
24 hours R.T. ASTM D570
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
Positive Mold; ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 55.0 MPa
7980 psi
ASTM D651
Flexural Strength 97.0 MPa
14100 psi
ASTM D790
Flexural Modulus 11.0 GPa
1600 ksi
ASTM D790
Compressive Strength 150 MPa
21800 psi
ASTM D695
Izod Impact, Notched 1.103 J/cm
2.066 ft-lb/in
ASTM D256A
Thermal Properties Metric English Comments
CTE, linear 18.0 µm/m-°C

@Temperature 20.0 °C
 10.0 µin/in-°F

@Temperature 68.0 °F
 ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 177 °C
351 °F
ASTM D648
Electrical Properties Metric English Comments
Dielectric Strength 12.8 kV/mm
325 kV/in
Short Time; Dry; ASTM D149
Processing Properties Metric English Comments
Mold Temperature 150 - 175 °C
302 - 347 °F